Large area and highly aligned polymer semiconductor sub-microwires were fabricated using the coaxial focused electrohydrodynamic jet printing technology. As indicated by the results, the sub-microwire arrays have smooth morphology, well reproducibility and controllable with a width of ~110 nm. Analysis shows that the molecular chains inside the sub-microwires mainly exhibited edge-on arrangement and the π-stacking direction (010) of the majority of crystals is parallel to the long axis of the sub-microwires. Sub-microwires based organic field effect transistors showed high mobility with an average of 1.9 cm2 V−1 s−1, approximately 5 times higher than that of thin film based organic field effect transistors. In addition, the number of sub-microwires can be conveniently controlled by the printing technique, which can subsequently concisely control the performance of organic field effect transistors. This work demonstrates that sub-microwires fabricated by the coaxial focused electrohydrodynamic jet printing technology create an alternative path for the applications of high-performance organic flexible device.
Patterning of semiconductor polymers is pertinent to preparing and applying organic field-effect transistors (OFETs). In this study, coaxial focused electrohydrodynamic jet printing (high resolution, high speed, and convenient) was used...
Electrohydrodynamic jet (e-jet) printing is a modern and decent fabrication method widely used to print high-resolution versatile microstructures with features down to 10 μm. It is currently difficult to break nanoscale resolution (<100 nm) due to limitations of fluid properties, voltage variations, and needle shapes. This paper presents developments in drop-on-demand e-jet printing based on a phase-field method using a novel combined needle and straight electrode to print on a flexible PET substrate. Initially, the simulation was performed to form a stable cone jet by coupling an innovative straight electrode parallel to a combined needle that directs the generation of droplets at optimized parameters, such as f = 8.6 × 10−10 m3s−1, Vn = 9.0 kV, and Vs = 4.5 kV. Subsequently, printing experiments were performed using optimized processing parameters and all similar simulation conditions. Microdroplets smaller than 13 μm were directly printed on PET substrate. The model is considered unique and powerful for printing versatile microstructures on polymeric substrates. The presented method is useful for MEMS technology to fabricate various devices, such as accelerometers, smartphones, gyroscopes, sensors, and actuators.
Polymer nanowire (NW) organic field-effect transistors (OFETs) integrated on highly aligned large-area flexible substrates are candidate structures for the development of high-performance flexible electronics. This work presents a universal technique, coaxial focused electrohydrodynamic jet (CFEJ) printing technology, to fabricate highly aligned 90-nm-diameter polymer arrays. This method allows for the preparation of uniformly shaped and precisely positioned nanowires directly on flexible substrates without transfer, thus ensuring their electrical properties. Using indacenodithiophene-co-benzothiadiazole (IDT-BT) and poly(9,9-dioctylfluorene-co-benzothiadiazole) (F8-BT) as example materials, 5 cm2 arrays were prepared with only minute size variations, which is extremely difficult to do using previously reported methods. According to 2D-GIXRD analysis, the molecules inside the nanowires mainly adopted face-on π-stacking crystallite arrangements. This is quite different from the mixed arrangement of thin films. Nanowire-based OFETs exhibited a high average hole mobility of 1.1 cm2 V−1 s−1 and good device uniformity, indicating the applicability of CFEJ printing as a potential batch manufacturing and integration process for high-performance, scalable polymer nanowire-based OFET circuits. This technique can be used to fabricate various polymer arrays, enabling the use of organic polymer semiconductors in large-area, high-performance electronic devices and providing a new path for the fabrication of flexible displays and wearable electronics in the future.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.