The cellular microenvironment plays an integral role in improving the function of microengineered tissues. Control of the microarchitecture in engineered tissues can be achieved through photopatterning of cell-laden hydrogels. However, despite high pattern fidelity of photopolymerizable hydrogels, many such materials are not cell-responsive and have limited biodegradability. Here we demonstrate gelatin methacrylate (GelMA) as an inexpensive, cell-responsive hydrogel platform for creating cell-laden microtissues and microfluidic devices. Cells readily bound to, proliferated, elongated and migrated both when seeded on micropatterned GelMA substrates as well as when encapsulated in microfabricated GelMA hydrogels. The hydration and mechanical properties of GelMA were demonstrated to be tunable for various applications through modification to the methacrylation degree and gel concentration. Pattern fidelity and resolution of GelMA was high and it could be patterned to create perfusable microfluidic channels. Furthermore, GelMA micropatterns could be used to create cellular micropatterns for in vitro cell studies or 3D microtissue fabrication. These data suggest that GelMA hydrogels could be useful for creating complex, cell-responsive microtissues, such as endothelialized microvasculature, or for other applications that requires cell-responsive microengineered hydrogels.

In this paper, we have developed a method to produce poly(lactic- co-glycolic acid) (PLGA) microfibers within a microfluidic chip for the generation of 3D tissue engineering scaffolds. The synthesis of PLGA fibers was achieved by using a polydimethylsiloxane (PDMS)-based microfluidic spinning device in which linear streams of PLGA dissolved in dimethyl sulfoxide (DMSO) were precipitated in a glycerol-containing water solution. By changing the flow rate of PLGA solution from 1 to 50 microL/min with a sheath flow rate of 250 or 1000 microL/min, fibers were formed with diameters that ranged from 20 to 230 microm. The PLGA fibers were comprised of a dense outer surface and a highly porous interior. To evaluate the applicability of PLGA microfibers generated in this process as a cell culture scaffold, L929 fibroblasts were seeded on the PLGA fibers either as-fabricated or coated with fibronectin. L929 fibroblasts showed no significant difference in proliferation on both PLGA microfibers after 5 days of culture. As a test for application as nerve guide, neural progenitor cells were cultured and the neural axons elongated along the PLGA microfibers. Thus our experiments suggest that microfluidic chip-based PLGA microfiber fabrication may be useful for 3D cell culture tissue engineering applications.