This report was carried out to study experimentally the water-assisted injection molding process of glass fiber-reinforced polyamide-6 (Nylon-6) composites. Experiments were carried out on an 80 ton injection molding machine equipped with a lab scale water injection system, which included a water pump, a water injection pin, a pressure accumulator, a water tank equipped with a temperature regulator, and a control circuit. The materials used were Nylon and 30% glass fiber-filled Nylon composites. A spiral mold cavity was used to mold the composites. After molding, the lengths of water penetration in molded parts were measured. The effects of different processing parameters on the lengths of water penetration were determined: melt temperature, mold temperature, melt-filling speed, short-shot size, water pressure, water temperature, water hold, and water injection delay time. Mechanical property tests were performed on the water-assisted injection molded parts. X-ray diffraction was also employed to identify the structural parameters of the materials. In addition, the in-mold temperature distribution of the polymeric materials during the cooling process was measured. Irregular water penetration in molded parts was observed, and water temperature was found to affect the crystallinity distribution of molded parts. Nevertheless, its effects on the tensile properties of molded materials were relatively limited.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.