The purpose of the present study is to evaluate the fracture resistance and the fit of CAD-CAM produced inlay-retained fixed partial dentures. Eighteen experimental groups were generated according to different CAD-CAM ceramic materials (zirconia, lithium disilicate, and zirconia-reinforced lithium silicate), different connector dimensions (12, 14, and 16 mm 2 ), and application of thermomechanical-aging (1,200,000 cycles of cyclic loading with simultaneous thermal cycling). Gap values of thermomechanicallyaged groups were measured by using periapical radiographs. Then, the specimens were tested for fracture resistance and failure types were examined. The results were statistically analyzed (α=0.05). Higher gap values were observed after aging. Zirconia showed the highest fracture resistance values among the most of the experimental groups. In non-aged groups, the most frequent failure type was decementation in zirconia group. In the aged groups, the most frequent failure type was molar connector fracture. Thermomechanicalaging increased the gap values and decreased the fracture resistance values.
Protetik restorasyonlarda sıklıkla kullanılan metal ve seramik materyallerin sahip olduğu bazı olumsuz özellikler nedeniyle alternatif materyal olarak polimerlerin kullanımı gündeme gelmektedir. Yüksek performanslı polimerlerden poliarileterketon ailesine ait yarı kristal yapıdaki polietereterketon materyali, medikal olarak kullanılmasından sonra diş hekimliği alanında da kullanılmaya başlanmıştır. Kimyasal olarak inert olması, yüksek mekanik dayanımı, aşınmaya dirençli ve hafif olması ile özellikle protetik tedavilerde yerini almıştır. Polietereterketon, inley, onley endokron restorasyonlarda, kron ve köprülerin altyapılarında, hareketli protezlerin altyapılarında, implant materyali olarak ve implant üstü sabit ve hareketli protezlerde ve ayrıca oklüzal splint yapımında kullanılabilmektedir. Bu derlemede Polietereterketon materyalinin yapısı, özellikleri ve protetik restorasyonlarda kullanım şekilleri anlatılmaktadır.
Dijital diş hekimliğinin hızlı bir şekilde gelişmesi bilgisayar destekli tasarım ve üretim sürecinin özellikle protetik alanda geniş kullanım alanı bulmasını sağlamıştır. CAD-CAM uygulamaları, protetik restorasyonların hem hekim hem de hasta açısından konforlu ve hızlı bir şekilde hazırlanmasına olanak tanır. Günümüzde materyal çeşitliliğinin artmasıyla minimal invaziv restorasyonların pratik bir şekilde üretilmesi mümkün olmaktadır. “Hasta başı” uygulamaları tek seansta restorasyonun tamamlanabileceği materyalleri ve dijital sistemleri tanımlamaktadır. Başarılı restorasyonlar için dijital sistemleri doğru kullanmak ve mevcut restoratif materyalleri iyi tanıyarak her vakaya uygun materyal seçimini yapabilmek gerekmektedir. Bu çalışmada güncel dijital sistemler ve hasta başı uygulamalarında kullanılabilen restoratif materyal çeşitlerinin anlatılması amaçlanmaktadır.
Objective: The objective of this study was to investigate the effects of liquid coloring in different dipping times and finishing procedures on color difference of precolored and liquid-colored monolithic zirconia ceramics. Materials and Methods: 240 zirconia specimens were divided according to shades of coloring liquid (A1, A2, and A3), dipping time (3, 5, and 7 minutes), and surface finishing procedures (glaze and mechanical polishing) (n=10). CIE L*, a*, and b* values of the specimens were measured and color differences (ΔE) were calculated. The data were analyzed with three-way analysis of variance (ANOVA) and Tukey HSD test (α=.05). Results: Coloring with liquids, dipping time, and finishing procedures significantly affected the CIE L*, a*, and b* values (P<.001). Dipping in coloring liquids decreased the a* and b* values. Higher L* values were obtained in glazing groups than mechanical polishing groups. The ΔE values among the experimental groups were varied from 7.10 to 27.52. The highest color difference was observed in 7 min dipping in A3 liquid and mechanically polished group. Conclusion: The color difference between the precolored and liquid-colored zirconia ceramics are not in acceptable limits. Dipping in coloring liquids and surface finishing affect the color of liquid-colored monolithic zirconia.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.