Antibacterial cerium-doped hydroxyapatite (Ce-HAp) layers have been researched sparingly in recent years. The Ce-HAp powder, Ca10−xCex(PO4)6(OH)2 with xCe = 0.05, was obtained by an adapted chemical co-precipitation method at room temperature. The target was prepared using the Ce-HAp (xCe = 0.05) powder sintered in air at 600 °C. The coatings on the Ti substrate were generated in plasma using a radio frequency (RF) magnetron sputtering discharge in an Ar gas flow in a single run. To collect the most complete information regarding the antimicrobial activity of cerium-doped hydroxyapatite with xCe = 0.05, (5Ce-HAp), antimicrobial studies were carried out both on the final suspensions and on the coated surfaces. The target was tested using ultrasound measurement, transmission electron microscopy (TEM), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), glow-discharge optical emission spectroscopy (GDOES), and X-ray photoelectron spectroscopy (XPS). The present study exhibited for the first time results of the homogeneous coatings of hydroxyapatite doped with cerium using a radio frequency magnetron sputtering technique. In addition, this study highlighted for the first time the stability of the cerium-doped hydroxyapatite gels used in the creation of the coating. Ultrasound measurements on the concentrated suspension of 5Ce-HAp showed a good stability compared to double distilled, water which was chosen as the reference fluid. Particles with spherical shape were observed by both TEM and SEM analysis. The broadening of the IR bands in the IR spectrum of the 5Ce-HAp film in comparison with the IR spectrum of the precursor target indicate the formation of interlinked bonds into the layer bulk. XPS analysis revealed that the mixture of Ce3+ and Ce4+ ions in the hydroxyapatite (HAp) structure of the coatings could be due to the deposition process. The surface of 5Ce-HAp coatings was homogenous with particles having a spherical shape. A uniform distribution of all the constituent elements on the surface the 5Ce-HAp layer was revealed. The antimicrobial assays proved that both 5Ce-HAp suspensions and 5Ce-HAp coatings effectively inhibited the development of colony forming units (CFU) for all the tested microbial strains. Moreover, the antimicrobial assays emphasized that the 5Ce-HAp suspensions had a biocide effect against Escherichia coli (E. coli) and Candida albicans (C. albicans) microbial strains after 72 h of incubation.

No abstract

Five Cu(x)CeMgAlO mixed oxides with different copper contents (x) ranging from 6 to 18 at. % with respect to cations, but with fixed 10 at. % Ce and Mg/Al atomic ratio of 3, were prepared by thermal decomposition of LDH precursors at 750 °C. Cu(15)CeMgAlO was also calcined at 550 and 650 °C. They were characterized by XRD, SEM-EDX, nitrogen adsorption/desorption, H2-TPR, XPS and DR-UV-Vis techniques. Their catalytic properties in the total oxidation of methane were evaluated and compared with those of an industrial Pd/Al2O3 catalyst. Cu(15)CeMgAlO was the most active catalyst in this series, with a T50 value of only ca. 45 °C higher than that of Pd/Al2O3. This difference becomes as low as ca. 25 °C for the Cu(15)CeMgAlO system calcined at 550 °C. The excellent stability on stream of the Cu(15)CeMgAlO catalyst was evidenced.

Silica-based bioactive glasses (SBG) hold great promise as bio-functional coatings of metallic endo-osseous implants, due to their osteoproductive potential, and, in the case of designed formulations, suitable mechanical properties and antibacterial efficacy. In the framework of this study, the FastOs®BG alkali-free SBG system (mol%: SiO2—38.49, CaO—36.07, P2O5—5.61, MgO—19.24, CaF2—0.59), with CuO (2 mol%) and Ga2O3 (3 mol%) antimicrobial agents, partially substituting in the parent system CaO and MgO, respectively, was used as source material for the fabrication of intentionally silica-enriched implant-type thin coatings (~600 nm) onto titanium (Ti) substrates by radio-frequency magnetron sputtering. The physico-chemical and mechanical characteristics, as well as the in vitro preliminary cytocompatibility and antibacterial performance of an alkali-free silica-rich bio-active glass coating designs was further explored. The films were smooth (RRMS < 1 nm) and hydrophilic (water contact angle of ~65°). The SBG coatings deposited from alkali-free copper-gallium co-doped FastOs®BG-derived exhibited improved wear performance, with the coatings eliciting a bonding strength value of ~53 MPa, Lc3 critical load value of ~4.9 N, hardness of ~6.1 GPa and an elastic modulus of ~127 GPa. The Cu and Ga co-doped SBG layers had excellent cytocompatibility, while reducing after 24 h the Staphylococcus aureus bacterial development with 4 orders of magnitude with respect to the control situations (i.e., nutritive broth and Ti substrate). Thereby, such SBG constructs could pave the road towards high-performance bio-functional coatings with excellent mechanical properties and enhanced biological features (e.g., by coupling cytocompatibility with antimicrobial properties), which are in great demand nowadays.

The objective of the present study is the valorization of natural resources and the recycling of vegetal wastes by converting them into novel plasmonic bio-active hybrids. Thus, a “green” approach was used to design pectin-coated bio-nanosilver. Silver nanoparticles were generated from two common garden herbs (Mentha piperita and Amaranthus retroflexus), and pectin was extracted from lemon peels. The samples were characterized by the following methods: Ultraviolet–visible (UV-Vis) absorption spectroscopy, Fourier Transform Infrared (FT-IR), X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), dynamic light scattering (DLS), Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM)–Energy-dispersive X-ray Spectroscopy (EDX), and zeta potential measurements. Microscopic investigations revealed the spherical shape and the nano-scale size of the prepared biohybrids. Their bioperformances were checked in terms of antioxidant and antibacterial activity. The developed plasmonic materials exhibited a strong ability to scavenge short-life (96.1% ÷ 98.7%) and long-life (39.1% ÷ 91%) free radicals. Microbiological analyses demonstrated an impressive antibacterial effectiveness of pectin-based hybrids against Escherichia coli. The results are promising, and the obtained biomaterials could be used in many bio-applications, especially as antioxidant and antimicrobial biocoatings.