In the short term, MTBS values were material and dental-substrate dependent. After aging, a decrease in bonding effectiveness was observed in all materials, with nanoleakage at the adhesive/dentin interface. The bonding of the UAs was equal or inferior to that of the conventional restorative systems when applied to either substrate and after either storage period.

Both MMAs tested can be considered effective alternatives for bonding to sandblasted indirect resin composite after aging, as they showed similar bond performance to that of the control group. However, separate bottles of silane bonding resin showed higher MSBS values and more durable bonding for etched glass-based ceramic.

No abstract

No abstract

Objective: The aim is to evaluate the effect of violet light (VL) and nonthermal atmospheric plasma (NTAP) combined with or without 35% hydrogen peroxide (HP) and 37% carbamide peroxide (CP).Methods: Bovine crowns were divided into (n = 10) VL, VL/HP, VL/CP, NTAP, NTAP/ HP, NTAP/CP, HP, CP, and C (control) groups. Color and whiteness change (CIELAB-ΔE ab, CIEDE2000-ΔE 00 , whiteness index-ΔWI D ), color parameters (ΔL, Δa, and Δb), and intrapulpal concentration (μL/mL) of HP were assessed by spectrophotometry.Scanning electron microscopy evaluated the morphology of enamel surface. Data were analyzed by two-way analysis of variance and Tukey (ΔE ab , ΔE 00 , ΔWI D , ΔL, and μL/mL) and Kruskal-Wallis and Mann-Whitney tests (Δa and Δb, α = 5%).Results: VL increased ΔE ab and ΔWI D of CP (P < .05). VL and NTAP alone resulted in perceptible color and whiteness change, but lower than those in the gel-treated groups (P < .05). Activation modes increased ΔL compared with that of C, but only VL enhanced Δb when applied alone or combined with CP. VL and NTAP did not increase HP diffusion (P > .05) or cause alterations in enamel morphology. However, HP and CP promoted topographical changes.Conclusion: VL and NTAP changed color to a lesser extent than bleaching gels. VL produced supplementary effectiveness only for CP (ΔE ab and ΔWI D ), without increasing HP diffusion or changing enamel morphology. Clinical Significance: Although violet LED light and nonthermal atmospheric plasma (NTAP) promoted in vitro perceptible bleaching without compromising enamel morphology, bleaching gels (hydrogen peroxide and carbamide peroxide) were more Part of this work was presented during poster session of the Annual Meeting

No abstract

SUMMARY Objectives: This study evaluated the effect of toothbrushing with a dentifrice on gloss, roughness profile, surface roughness, and wear of conventional and bulk-fill resin-based composites. Methods and Materials: Gloss and surface roughness of resin-based composites (RBCs; Admira Fusion X-tra, Aura Bulk Fill, Filtek Bulk Fill Flowable, Filtek Bulk Fill Posterior Restorative, Filtek Supreme Ultra, Herculite Ultra, Mosaic Enamel, SDR flow+, Sonic Fill 2, Tetric EvoFlow Bulk Fill and Tetric EvoCeram Bulk Fill) were analyzed before and after brushing; the roughness profile and wear were also determined after toothbrushing. Representative three-dimensional images of the surface loss and images comparing the unbrushed and brushed surfaces were also compared. Analysis of variance and Tukey post hoc tests were applied (α=0.05) to the gloss, surface roughness, roughness profile, and surface loss data. Pearson's correlation test was used to determine the correlation between gloss and surface roughness, surface loss and percentage of gloss decrease after brushing, and surface loss and surface roughness after brushing. Results: For all RBCs tested after 20,000 brushing cycles, the gloss was reduced and the surface roughness increased (p&lt;0.05). However, the roughness profile and the amount of surface loss were dependent on the RBC brand. Admira Fusion X-tra, Aura, Tetric EvoCeram Bulk Fill, and Tetric EvoFlow Bulk Fill showed the deepest areas of wear (p&lt;0.05). A significant negative correlation was found between gloss and surface roughness, and a weak correlation was found between the decrease in gloss and the extent of surface loss, and any increase in surface roughness and the surface loss. Conclusions: Toothbrushing with a dentifrice reduced the gloss, increased the surface roughness, and caused loss at the surface of all the RBCs tested. Considering all the properties tested, Mosaic Enamel exhibited excellent gloss retention and a low roughness profile and wear, while Admira Fusion X-tra exhibited the greatest decrease in gloss, the highest roughness profile, and the most wear.

ObjectiveTo evaluate the effects of human saliva decontamination protocols on bond strength of resin cement to zirconia (Y‐PSZ), wettability, and microbial decontamination.Materials and methodsZirconia plates were sandblasted and divided into (a) not contaminated, (b) contaminated with human saliva and: (c) not cleaned, (d) cleaned with air‐water spray, (e) cleaned with 70% ethanol, (f) cleaned with Ivoclean, or (g) cleaned with nonthermal atmospheric plasma (NTAP). The wettability and microbial decontamination of the surfaces were determined after saliva contamination or cleaning. Monobond Plus (Ivoclar Vivadent) was applied after cleaning, followed by Variolink LC (Ivoclar Vivadent). The samples were stored 1 week before shear bond strength (SBS) testing, and data (SBS and wettability) were analyzed by one‐way analysis of variance and Tukey test (α = .05).ResultsSaliva contamination reduced SBS to zirconia compared to not contaminated. Both Ivoclean and NTAP produced higher SBS compared to not cleaned and were not significantly different from the not contaminated. Ivoclean produced the highest contact angle, and NTAP the lowest. With the exception of using just water‐spray, all cleaning protocols decontaminated the specimens.ConclusionsBoth Ivoclean and NTAP overcame the effects of saliva contamination, producing an SBS to zirconia comparable to the positive control.Clinical significanceDental ceramics should be cleaned prior to resin cementation to eliminate the effects of human saliva contamination, and Ivoclean and NTAP are considered suitable materials for this purpose.