A facile and flexible synthesis for colloidal molecules with well-controlled shape and tunable patchiness is presented. Cross-linked polystyrene spheres with a liquid protrusion were found to assemble into colloidal molecules by coalescence of the liquid protrusions. Similarly, cross-linked poly(methyl methacrylate) particles carrying a wetting layer assembled into colloidal molecules by coalescence of the wetting layer. Driven by surface energy, a liquid droplet on which the solid spheres are attached is formed. Subsequent polymerization of the liquid yields a wide variety of colloidal molecules as well as colloidosomes with tunable patchiness. Precise control over the topology of the particles has been achieved by changing the amount and nature of the swelling monomer as well as the wetting angle between the liquid and the seed particles. The overall cluster size can be controlled by the seed size as well as the swelling ratio. Use of different swelling monomers and/or particles allows for chemical diversity of the patches and the center. For low swelling ratios assemblies of small numbers of seeds resemble clusters that minimize the second moment of the mass distribution. Assemblies comprised of a large number of colloids are similar to colloidosomes exhibiting elastic strain relief by scar formation.

Core-shell polystyrene-silica spheres with diameters of 800 nm and 1.9 microm were synthesized by soap-free emulsion and dispersion polymerization of the polystyrene core, respectively. The polystyrene spheres were used as templates for the synthesis of silica shells of tunable thickness employing the Stöber method [Graf et al. Langmuir 2003, 19, 6693]. The polystyrene template was removed by thermal decomposition at 500 degrees C, resulting in smooth silica shells of well-defined thickness (15-70 nm). The elastic response of these hollow spheres was probed by atomic force microscopy (AFM). A point load was applied to the particle surface through a sharp AFM tip, and successively increased until the shell broke. In agreement with the predictions of shell theory, for small deformations the deformation increased linearly with applied force. The Young's modulus (18 +/- 6 GPa) was about 4 times smaller than that of fused silica [Adachi and Sakka J. Mater. Sci. 1990, 25, 4732] but identical to that of bulk silica spheres (800 nm) synthesized by the Stöber method, indicating that it yields silica of lower density. The minimum force needed to irreversibly deform (buckle) the shell increased quadratically with shell thickness.

The synthesis of nanosized superparamagnetic hematite particles by dissolving ferric salts in hydrochloric acid and heating at 100• C is described. A hydrolysis reaction causes the formation of hematite particles. The influence of the sequence of additions on the resulting precipitates was studied using TEM and XRD. The magnetic behavior was characterized by magnetization measurements. It was found that small changes in the reaction conditions led to remarkable changes in final size and shape of the hematite crystallites. A well-defined subrounded morphology and an average diameter of 41 nm were obtained for superparamagnetic hematite particles. This is the largest size reported thus far for superparamagnetic hematite particles. C 2002 Elsevier Science (USA)

We describe the synthesis and characterization of stable suspensions of monodisperse fluorescently labeled silica dumbbell particles. Pure dispersions of silica dumbbells with center-to-center lengths from 174 nm to 2.3 microm were produced with a variety of aspect ratios. Individual particles in concentrated dispersions of these particles could be imaged with confocal microscopy. These particles can be used as a colloidal model system for addressing fundamental questions about crystal and glass formation of low-aspect-ratio anisotropic particles. They also have potential in photonic applications and electro-optical devices.