No abstract

No abstract

The coordination polymer [Zn(BDC)(H(2)O)(2)](n) was tested for extraction of pyrimethanil, ametryn, dichlofluanid, tetraconazole, flumetralin, kresoxim-methyl and tebuconazole from the medicinal plant Hyptis pectinata, with analysis using gas chromatography-mass spectrometry in selected ion monitoring mode (GC/MS, SIM). Experiments carried out at different fortification levels (0.1, 0.5 and 1.0 μg g(-1)) resulted in recoveries in the range 73-97%, and RSD values were between 5 and 12% for the [Zn(BDC)(H(2)O)(2)](n) sorbent. Detection and quantification limits ranged from 0.02 to 0.07 μg g(-1) and from 0.05 to 0.1 μg g(-1), respectively, for the different pesticides studied. The method developed was linear over the range tested (0.04-14.0 μg g(-1)), with correlation coefficients ranging from 0.9987 to 0.9998. Comparison between [Zn(BDC)(H(2)O)(2)](n) and the commercial phase C(18)-bonded silica showed good performance of the [Zn(BDC)(H(2)O)(2)](n) polymeric sorbent for the pesticides tested.

This manuscript reports the first example of up-conversion properties involving Yb 3+ and Tb 3+ ions in five isostructural Lanthanide-Organic Frameworks (LnOFs), herein designated as UCMarker-1 to UCMarker-5, respectively, and their application as optical probes for the identification of gunshot residues (GSRs) and the ammunition encryption procedure. The excitation of the Yb 3+ 2 F 7/2 « 2 F 5/2 transition (980 nm) at room temperature leads to visible up-conversion (UC) emission of Tb 3+ 5 D 4 A 7 F J . The GSR and lead-free primer residues are easily identified upon UV radiation (l = 254 nm). These results prove that the exploration of LnOFs to identify GSR is attractive for the identification of ammunition origins or caliber recognition.

No abstract

Magnesium complex hydrides as Mg2FeH6 are interesting phases for hydrogen storage in the solid state, mainly due to its high gravimetric and volumetric densities of H2. However, the synthesis of this hydride is not trivial because the intermetallic phase Mg2Fe does not exist and Mg and Fe are virtually immiscible under equilibrium conditions. In this study, we have systematically studied the influence of the most important processing parameters in reactive milling under hydrogen (RM) for Mg2FeH6 synthesis: milling time, ball-to-powder weight ratio (BPR), hydrogen pressure and type of mill. Low cost 2Mg-Fe mixtures were used as raw materials. An important control of the Mg2FeH6 direct synthesis by RM was attained. In optimized combinations of the processing parameters, very high proportions of the complex hydride could be obtained.

X-ray powder diffraction data collected in transmission and high-throughput geometries were used to analyze form I of atorvastatin. The X-ray wavelength of the synchrotron radiation used in this study was determined to be λ=1.3771 Å. Form I of atorvastatin was found to be triclinic with space group P1 and unit cell parameters a=5.4568(2) Å, b=9.8887(4) Å, c=30.3091(9) Å, α=76.801(3)°, β=99.177(5)°, γ=105.318(5)°, V=1527.1(1) Å3, Z=1, and M=1209.41 g mol−1 Alternatively, another unit cell dimension can be used to describe the same P1 crystal with a=5.4564(2) Å, b=9.8883(4) Å, c=29.6555(8) Å, α=95.745(3)°, β=94.297(5)°, γ=105.327(5)°, and V=1526.8(1) Å3.

. Glass ionomer cements are glass and polymer composite materials. These materials currently find use in dentistry. The purpose of this work is to obtain glass powders based on the composition 4.5SiO 2 -3Al 2 O 3 -2CaO to be used in dentistry. The powders were prepared by a chemical route at 700 0 C. The properties of glass ionomer cements obtained from powders prepared at 700 ºC were studied. Diametral tensile strength and microhardness were evaluated for the experimental glass ionomer cements and a commercial material. It was concluded that the properties of experimental cements were similar to those of the commercial ones.Keywords: cements; dental; glass. INTRODUÇÃOCimento de ionômero de vidro (CIV) é um material compósito vidro/polímero, no qual as partículas de vidro têm função de material de preenchimento e são fonte de cátions para formação de ligações cruzadas com as cadeias poliméricas. Os cimentos são formados pela mistura de partículas vítreas com solução aquosa de áci-dos poliméricos orgânicos (geralmente ácido poliacrílico) 1,2 . Quando as partículas de vidro do tipo cálcioaluminosilicato são misturadas com solução aquosa de ácido poliacrílico forma-se uma pasta, que pode ser facilmente manipulada pelo dentista e usada em várias aplicações odontológicas, como cimentação de dispositivos protéticos, forração de cavidades e nas restaurações 3 . Os CIV adquirem presa inicial via reação de neutralização do tipo ácido/base entre os seus componentes. O processo envolve a hidrólise ácida das ligações Si -O -Al da rede vítrea, resultando na liberação dos cátions Ca 2+ e Al 3+ e na formação de ácido ortosilícico, o qual se polimeriza formando sílica gel 4,5 . Os cátions extraídos da rede vítrea Ca 2+ e Al 3+ são quelados pelos grupos carboxílicos, presentes na estrutura polimérica do ácido orgânico, formando sais de poliacrilato e iniciando a "pega" da pasta vidro/ ácido por geleificação 1 . Dessa maneira, o cimento obtido é constituído de partículas vítreas, com superfície revestida por sílica gel, e que estão presentes em uma matriz formada pelos sais de poliacrilato, os quais são responsáveis pelo endurecimento dos cimentos.Os CIV apresentam certas propriedades, tais como adesão à estrutura dentária, valor do coeficiente de expansão térmico linear similar ao do dente e biocompatibilidade com os tecidos dentários [6][7][8] . Essas propriedades propiciam o uso desses cimentos em Dentística Restauradora como agentes cimentantes, para forramento de cavidades, preenchimento de dentes anteriores e, também, como cimentos ósseos 9 . Os sistemas vítreos mais utilizados em Odontologia como formadores de cimentos de ionômero de vidro são os baseados no sistema ternário SiO 2 -Al 2 O 3 -CaO 2,4,5 e apresentam razão molar Al:Si igual ou superior a 1:2. A partir desse sistema originaram-se outros mais complexos, pela inclusão de novos componentes para conferir ao cimento odontológico propriedades melhores. Por ex., a maioria dos pós contêm em suas formulações óxidos de BaO ou SrO, modificadores ópticos, que conferem ao ...