AimThe aim of this study was to evaluate the influence of different concentrations of two photoinitiators and one co-initiator on the flexural strength (FS) and elastic modulus (E) of experimental resin cements.Materials and methodsA mixture containing BisGMA, TEGDMA, and barium-aluminum-silicate (BaAlSi) and silanized colloidal silica (SiO2) filler particles was prepared with two photoinitiators, viz. camphorquinone (CQ) and bisacylphosphine oxide (BAPO). Dimethylaminoethyl methacrylate (DMAEMA) was used as co-initiator. Thirty groups (n=10) were formulated with different photoinitiator systems (CQ/DMAEMA and BAPO/DMAEMA) and concentrations (wt%) of photoinitiator and co-initiator. The photoactivation was carried out for 20 s with a light-emitting diode (LED, Bluephase, Ivoclar Vivadent) with irradiance of 1200 mW/cm2. The FS and E were obtained in a three-point bending test on a universal testing machine (0.5 mm/min). Data were subjected to the Kolmogorov-Smirnov normality test, followed by two-way ANOVA and Tukey’s test (α=0.05).ResultsNo polymerization occurred in the CQ groups without DMAEMA (0 wt%). DMAEMA 0.5 %wt and 1 %wt groups showed statistically similar FS and E results for CQ and BAPO, except for CQ 0.3 wt% (FS), CQ 0.9wt% (E) and BAPO 1.76 wt% (FS and E) for DMAEMA 0.5 %wt. No significant difference was found for FS and E values for different concentrations of photoinitiators, except for CQ 0.25 wt% (FS and E) and BAPO 0.25 wt% (E) that showed the lowest values.ConclusionThe wt% of the photoinitiators and co-initiator influenced the mechanical properties and the performance of CQ was dependent on the DMAEMA concentration. BAPO can be used as substitute for the conventional CQ/DMAEMA photoinitiator system.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.