The micellization of three tailor-made triblock copolymers, such as PB 100 -P2VP 100 -PEO 104 , PB 185 -P2VP 108 -PEO 154 , and PB 37 -P2VP 115 -PEO 241 , having similar total molecular weights and constant poly(2-vinylpyridine) (P2VP) sequence lengths, was investigated as a function of pH and sodium dodecyl sulfate (SDS) concentration. At pH 7 the formation of intermicellar aggregates was observed, especially for copolymers of low poly(ethylene oxide) (PEO) content. A pH decrease from 7 to 3 leads to a particle size increase due to the electrostatic repulsion of the protonated P2VP chains. The influence of the PEO sequence length was also observed for zeta potential values. At pH 3, in the absence of SDS, core-shell-corona micelles are formed whereas in the presence of small amount of SDS (degree of neutralization DN 5 0%-50%), a complex is formed between SDS and the protonated P2VP which leads to the shrinkage of the shell and thus to a decrease of the micellar sizes. For higher DN values, the micellar sizes increase due to the formation of large agglomerates and a transition occurs from a monomodal to a bimodal size distribution. Furthermore, it turned out that secondary aggregation, such as intermicellar aggregation, can completely be avoided if the degree of polymerization (DPn) of the water-soluble block is significantly higher than the DPn of the water-insoluble sequence.

The curcumin degradation represents a significant limitation for its applications. The stability of free curcumin (FC) and immobilized curcumin in complex particles (ComPs) based on different polysaccharides was studied under the action of several factors. Ultraviolet-visible (UV-VIS) and Fourier-transform infrared (FTIR) spectroscopy proved the FC photodegradation and its role as a metal chelator: 82% of FC and between 26% and 39.79% of curcumin within the ComPs degraded after exposure for 28 days to natural light. The degradation half-life (t1/2) decreases for FC when the pH increases, from 6.8 h at pH = 3 to 2.1 h at pH = 9. For curcumin extracted from ComPs, t1/2 was constant (between 10 and 13 h) and depended on the sample’s composition. The total phenol (TPC) and total flavonoids (TFC) content values increased by 16% and 13%, respectively, for FC exposed to ultraviolet light at λ = 365 nm (UVA), whereas no significant change was observed for immobilized curcumin. Antioxidant activity expressed by IC50 (µmoles/mL) for FC exposed to UVA decreased by 29%, but curcumin within ComPs was not affected by the UVA. The bovine serum albumin (BSA) adsorption efficiency on the ComPs surface depends on the pH value and the cross-linking degree. ComPs have a protective role for the immobilized curcumin.

Cross-linked chitosan (CS) films with aldehyde groups obtained by oxidation of carboxymethyl cellulose (CMC) with NaIO4 were prepared using different molar ratios between the CHO groups from oxidized carboxymethyl cellulose (CMCOx) and NH2 groups from CS (from 0.25:1 to 2:1). Fourier-transform infrared (FTIR) and nuclear magnetic resonance (NMR) spectroscopy demonstrated the aldehyde groups’ presence in the CMCOx. The maximum oxidation degree was 22.9%. In the hydrogel, the amino groups’ conversion index value increased when the -CHO/-NH2 molar ratio, cross-linking temperature, and time increased, while the swelling degree values decreased. The hydrogel films were characterized by scanning electron microscopy (SEM) and FTIR analysis. The curcumin encapsulation efficiency decreases from 56.74% to 16.88% when the cross-linking degree increases. The immobilized curcumin release efficiency (REf%) and skin membrane permeability were evaluated in vitro in two different pH solutions using a Franz diffusion cell, and it was found to decrease when the molar ratio -CH=O/NH2 increases. The curcumin REf% in the receptor compartment was higher at pH = 7.4 (18%- for the sample with a molar ratio of 0.25:1) than at pH = 5.5 (16.5%). The curcumin absorption in the skin membrane at pH = 5.5 (47%) was more intense than at pH = 7.4 (8.6%). The curcumin-loaded films’ antioxidant activity was improved due to the CS presence.