In this study, we evaluated the influence of nickel and cobalt concentrations in an electrochemical bath for a ternary Ni‐Co‐W coating alloy electrodeposition. The X‐ray diffraction indicated formation of amorphous coating alloys for higher Co concentration and a crystalline coating alloys for higher Ni concentration. Statistical evaluation showed a mathematical model connecting the increase of alloy deposition efficiency and the Ni and Co concentration in the electrochemical bath. Corrosion tests indicated that coating alloys with higher Ni concentration, which are crystalline alloys, showed higher polarization resistance (in NaCl 0.1 mol/L) indicating that composition can influence the corrosion resistance more than the crystallinity.

Neste trabalho foi realizada a caracterização eletroquímica de ligas ternárias de Ni-CoW , pelos métodos eletroquímicos de Tafel, com levantamento das curvas de polarização potenciodinâmica e Impedância Eletroquímica. Os resultados permitiram avaliar o desempenho das ligas de Ni-CoW em solução de NaCl como meio corrosivo, bem como, a maneira com que a resistência à corrosão é modificada pela composição química da liga.

As ligas de metálicas foram eletrodepositadas variando as concentrações de Ni e Co utilizadas no banho eletrolítico.O substrato utilizado foi de cobre com 2 cm de lado de um quadrado em um eletrodo rotatório. Os ensaios de eletrodeposição foram realizados com densidade de corrente 50 mA/cm2, tempertatura ambiente e rotação catódica de 20 rpm. Foram feitas análises de Difração de Raios X, para estudo da composição e cristalinidade, análises de Microscopia Eletrônica de Varredura e FTIR para análise da morfologia da superfície. Aplicou-se métodos matemáticos para o estudo da eficiência de deposição. A maior eficiência obtida foi de 15,69%.