A series of polyimide(PI) adhesives were synthesized from 2,2'-Bis [4-(4-aminophenoxy)phenyl] propane(BAPP), 4,4'-Diaminodiphenylmethane (MDA) and 3,3',4,4'-Benzophenonetetracarboxylic acid dianhydride (BTDA) via a two-step process. PI adhesives with different BAPP content were characterized in regard to their structure, thermal stability, mechanical properties and adhesive performance. Results showed that these PIs had excellent thermal stability, whose glass transition temperature (Tg) were around 300 C. While, superior dynamic mechanical behavior was observed, and the maximum loss factor declined with the increase of BAPP content. Single-lap shear strength of over 15.58 MPa at room temperature was obtained, and it remained high even at the temperature of 350 C. Factors that could affect bonding strength of these PI adhesives such as molar ratio of the diamine monomers, surface roughness of adherends and curing processes were investigated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.