Notched tensile tests of Ti-6Al-6V-2Sn welds, which were subjected to distinct post-weld heat treatments (PWHTs), were carried out in air at 150, 300 and 450°C. The results were compared with those of mill-annealed base metal (MB) specimens tested at same temperatures. The notched tensile strength (NTS) of the MB specimens decreased significantly with increasing temperature. Moreover, the welds with high hardness showed notch brittleness at room temperature but had a higher NTS than the MB specimen. The presence of grain boundary a layer promoted grain boundary shear, therefore, reduced its notch brittleness at room temperature for the weld with the PWHT at 704°C (the W-704 specimen). A lack of deformation compatibility at the interfaces between the a and b phases caused interfacial separations in the MB specimen as well as void formation in the W-704 specimen, leading to the low NTS of these specimens at elevated temperatures.KEY WORDS: notched tensile test; Ti-6Al-6V-2Sn; post-weld heat treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.