Dielectric breakdown of 7-Å-thick Al2O3 (111) films grown on Ni3Al(111) under ultrahigh vacuum conditions is induced by increasing the bias voltage on the scanning tunneling microscopy tip under constant current feedback. Breakdown is marked by the precipitous retreat of the tip from the surface, and the formation of an elevated feature in the scanning tunneling microscopy image, typically greater than 5 nm high and ∼100 nm in diameter. Constant height measurements performed at tip/sample distances of 1 nm or less yield no tip/substrate physical interaction, indicating that such features do not result from mass transport. Consistent with this, current/voltage measurements within the affected regions indicate linear behavior, in contrast to a band gap of 1.5 eV observed at unaffected regions of the oxide surface. A threshold electric field value of 11±1 MV cm−1 is required to induce breakdown, in good agreement with extrapolated values from capacitance measurements on thicker oxides.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.