This study was conducted to evaluate the resistance of heat-treated wood using the catalyst to decay caused by fungi for sapwood and heartwood of two tree species, Korean red pine (Pinus densiflora) and Japanese larch (Larix kaempferi), respectively. Wood samples were immersed for 10 min in sulfuric acid (7.5%) and then heat-treated at 130℃ for 90 min. Fomitopsis palustris, a brown-rot fungus, was used to examine the decay resistance of Korean red pine and Japanese larch wood. Weight and density of wood from the all conditions increased after heat treatment using the catalyst. Weight loss after decay resistance test was also dropped with a heat treatment. The lowest weight loss indicated at heat-treated heartwood of Japanese larch. Heat treatment using the catalyst effectively increased the resistance of wood to decay caused by fungi.
We investigated the functional characteristics of commercial wood charcoal in Korea and their application as functional raw materials. The areas of analysis were anatomical features, elementary composition, mineral composition, caloric values, anion and far-infrared ray emission, and moisture absorption capacity. Based on the analyses as above mentioned, it is considered that charcoal can be evaluated as functional raw material. In commercial wood charcoal in Korea, there were highly varied depending on manufacturing methods as black charcoal, white charcoal and mechanical charcoal and manufactures for elementary composition, mineral composition,
국내 시판용 목탄의 기능성 분석(Ⅱ)-481 -anion emission, far infrared ray emission. Especially, black charcoal showed lower moisture absorption capacity than white charcoal and mechanical charcoal. For charcoal as functional raw material, selective usage are needed based on the analyses of anatomical features, elementary composition, mineral composition, caloric values, anion and far-infrared ray emission, and moisture absorption capacity. Specific charcoal making methods for improving specific functionality, required as functional raw material, are necessary in further research.
We analyzed the basic characteristics and adsorption property of carbonized materials from thinning byproducts of major Korean wood species for evaluating as charcoal making raw material. Yield of charcoal was decreased with increasing the carbonization temperature for all wood species. Refining degrees was 9.0 at 400°C, 3.3∼5.0 at 600°C and 0 at 800°C, and was no-281-1)
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.