The experimental conditions for {111} twin formation in BaTiO3 were investigated. When BaTiO3 compacts without excess TiO2 were sintered either in an oxidizing atmosphere (air) or in a reducing atmosphere (95N2–5H2), no {111} twins formed within the BaTiO3 grains and no abnormal grain growth occurred. In contrast, many {111} twins were present within the abnormally grown grains in the excess‐TiO2‐containing BaTiO3 samples sintered in air, while no twins were observed in the excess‐TiO2‐containing samples sintered in 95N2–5H2. X‐ray diffraction analysis showed that excess TiO2 forms a Ba6Ti17O40 phase during sintering with the space group A2/a in air and a Ba6Ti17O40−x phase with the space group C in 95N2–5H2. It appears therefore that excess TiO2 and an oxidizing atmosphere are necessary for {111} twin formation in BaTiO3. These results may also indicate that the interface structure between BaTiO3 and Ba6Ti17O40 influences the twin formation.
Two series of experiments were performed to study the experimental conditions for the formation of {111} twins and related microstructures in barium strontium titanate ((Ba, Sr)TiO3). In the first series, the phase equilibria in the BaTiO3–SrTiO3–TiO2 system were determined. XRD and WDS analysis, done in the BaTiO3‐rich region, of 45(Ba,Sr)TiO3–10TiO2 samples annealed at 1250°C for 200 h in air showed that (Ba,Sr)TiO3 was in equilibrium with Ba6Ti17O40 (B6T17) and Ba4Ti13O30 phases with strontium solubility (Sr/(Ba + Sr)) of ∼0.02 and 0.20, respectively. In the second series the microstructures of samples consisting of a mixture of (Ba,Sr)TiO3 and 2.0 mol% TiO2, were observed after sintering at 1250°C for 100 h in air. {111} twins formed only in the samples with faceted B6T17 second phase particles, similar to the case of BaTiO3. In these samples, abnormal grain growth occurred in the presence of the {111} twins. In contrast, no {111} twins formed and no abnormal grain growth occurred in the samples containing second phase particles other than B6T17. With an increased substitution of strontium for barium, the aspect ratio of abnormal grains containing {111} twin lamellae was reduced. This result was attributed to a reduction in the relative stability of the {111} planes with the strontium substitution.
A structural transition of Ba6Ti17O40/BaTiO3 interfaces from faceted to rough was induced by reducing oxygen partial pressure in the atmosphere. As the oxygen partial pressure decreased, the number densities of {111} twins and abnormal grain decreased. TEM observation showed that the twin formation was governed only by the faceting of the interface. Experimental evidence of {111} twin‐assisted abnormal growth of faceted BaTiO3 grains was also obtained.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.