This study evaluated a simple and novel route to fabricate single-phase SnS thin films, consisting of the growth of smooth amorphous SnS2 films by atomic layer deposition at very low temperature using tetrakis(dimethylamino)tin {TDMASn, [(CH3)2N]4Sn} and hydrogen sulfide followed by H2 annealing at controlled higher temperatures. The properties of the SnS films fabricated by subjecting the amorphous as-grown SnS2 films deposited at 100 °C to post-H2 annealing at 360 °C were superior to those of the as-grown SnS films deposited at 200 °C in terms of their phase purity, optical band gap, adhesion, and surface roughness. Raman spectroscopy, x-ray diffraction, x-ray photoelectron spectroscopy, Rutherford backscattering spectrometry, and atomic force microscopy consistently showed that single-phase, stoichiometric crystalline (orthorhombic structure) SnS films (Sn/S ratio: ∼1), without any incorporated sulfur-rich tin sulfides, could be fabricated with a very low surface roughness [root mean square (RMS) roughness: ∼7 nm] using the proposed scheme. On the other hand, the as-grown SnS film at 200 °C still contained a small amount of SnS2 phase and its RMS surface roughness was as high as 16 nm. The optical band gap of the as-grown SnS film was 1.85 eV, whereas that of the annealed SnS film was ∼1.2 eV, confirming the latter's improved phase purity. The SnS film fabricated by H2 annealing was a p-type semiconductor with a carrier concentration of ∼2.3 × 1016/cm3 and a hole mobility of ∼15 cm2/V s. The present scheme to prepare high-quality SnS films might be useful for fabricating photovoltaic or solar conversion devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.