The inherent defective morphology of the physical vapor deposition (PVD) hard coatings limits their corrosion protective ability. We examined the impact of nitride‐based PVD coatings, including TiN, TiAlN, and CrN deposited on inert substrates by cathodic arc PVD method (CA‐PVD), on the galvanic corrosion of carbon steel. Their contribution was evaluated by zero‐resistance ammeter (ZRA) and electrochemical impedance spectroscopy (EIS) in 3.5 wt.% NaCl at pH 2 and 6, with and without aeration. The results indicated the prominent role of the coating type and the coupling environment on the generated galvanic currents. Immersion tests for the TiN‐, TiAlN‐, and CrN‐coated steel cross‐sections visually verified these results. The galvanic current contribution was distinct in environments where oxygen reduction is the dominant cathodic reaction. However, the layers' contribution to galvanic corrosion was minimal in deaerated acidic solutions, which is attributed to the high bonding strength of adsorbed intermediates to the coating surfaces.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.