Forty-one different polymer samples, collectively called the Polymer Erosion and Contamination Experiment (PEACE) Polymers, were exposed to the low Earth orbit (LEO) environment on the exterior of the International Space Station (ISS) for nearly 4 years as part of Materials International Space Station Experiment 2 (MISSE 2). The objective of the PEACE Polymers experiment was to determine the atomic oxygen erosion yield of a wide variety of polymeric materials after long-term exposure to the space environment. The polymers range from those commonly used for spacecraft applications, such as Teflon ® FEP, to more recently developed polymers, such as high temperature polyimide PMR (polymerization of monomer reactants). Additional polymers were included to explore erosion yield dependence upon chemical composition. The MISSE PEACE Polymers experiment was flown in MISSE Passive Experiment Carrier 2 (PEC 2), tray 1, attached to the exterior of the ISS Quest Airlock. It was exposed to atomic oxygen along with solar and charged particle radiation. MISSE 2 was successfully retrieved during a space walk on July 30, 2005 during Discovery's STS-114 Return to Flight mission. Details on the specific polymers flown, flight sample fabrication, pre-flight and post-flight characterization techniques, and atomic oxygen fluence calculations are discussed along with a summary of the atomic oxygen erosion yield results. The MISSE 2 PEACE Polymers experiment is unique because it has the widest variety of polymers flown in LEO for a long duration and was exposed to an unusually clean LEO spacecraft environment. This experiment provides extremely valuable erosion yield data for spacecraft design purposes.

Federal lab commercialization is explored: (1) by analyzing US government patents and (2) in a qualitative analysis of one NASA lab’s patents. Tests apply to three distinct sets of patents, 1963–94: NASA, all other US government, and a random sample of all US inventors’ patents. The federal patenting rate plummeted in the 1970s. Consistent with increasing commercialization, both NASA’s and other federal agencies’ rates recovered in the 1980s. The case study finds citations to be a valid but noisy measure of technology spillovers. Excluding ‘spurious’ cites, two‐thirds of cites to patents of NASA‐Lewis’ Electro‐Physics Branch were evaluated as involving spillovers.

Atomic oxygen, formed in Earth's thermosphere, interacts readily with many materials on spacecraft flying in low Earth orbit (LEO). All hydrocarbon based polymers and graphite are easily oxidized upon the impact of ∼4.5 eV atomic oxygen as the spacecraft ram into the residual atmosphere. The resulting interactions can change the morphology and reduce the thickness of these materials. Directed atomic oxygen erosion will result in the development of textured surfaces on all materials with volatile oxidation products. Examples from space flight samples are provided. As a result of the erosive properties of atomic oxygen on polymers and composites, protective coatings have been developed and are used to increase the functional life of polymer films and composites that are exposed to the LEO environment. The atomic oxygen erosion yields for actual and predicted LEO exposure of numerous materials are presented. Results of in-space exposure of vacuum deposited aluminum protective coatings on polyimide Kapton indicate high rates of degradation are associated with aluminum coatings on both surfaces of the Kapton. Computational modeling predictions indicate that less trapping of the atomic oxygen occurs, with less resulting damage, if only the space-exposed surface is coated with vapor deposited aluminum rather than having both surfaces coated.

The outer layer of Teflon® fluorinated ethylene propylene (FEP) multi-layer insulation (MLI) on the Hubble Space Telescope (HST) was observed to be significantly cracked at the time of the Second HST Servicing Mission (SM2), 6.8 years after HST was launched into low Earth orbit (LEO). Comparatively minor embrittlement and cracking were also observed in the FEP materials retrieved from solar-facing surfaces on the HST at the time of the First Servicing Mission (3.6 years exposure). After SM2, a failure review board was convened to address the problem of degradation of MLI on the HST. In order for this board to determine possible degradation mechanisms, it was necessary to consider all environmental constituents to which the FEP MLI surfaces were exposed. Based on measurements and various models, the environmental exposure conditions for the FEP surfaces on the HST were estimated, including: the number and temperature ranges of thermal cycles; equivalent sun hours; fluence and absorbed radiation dose of x-rays, trapped protons and electrons and plasma electrons and protons; and atomic oxygen (AO) fluence. This paper presents the environmental exposure conditions for FEP on the HST, briefly describing the possible roles of the environmental factors in the observed FEP embrittlement and providing references to the published works which describe in detail testing and analysis related to FEP degradation on the HST.

During the Hubble Space Telescope (HST) second servicing mission (SM2), degradation of unsupported Teflon ® FEP (fluorinated ethylene propylene), used as the outer layer of the multilayer insulation (MLI) blankets, was evident as large cracks on the telescope light shield. A sample of the degraded outer layer was retrieved during the mission and returned to Earth for ground testing and evaluation. The results of the Teflon ® FEP sample evaluation and additional testing of pristine Teflon ® FEP led the investigative team to theorize that the HST damage was caused by thermal cycling with deep-layer damage from electron and proton radiation which allowed the propagation of cracks along stress concentrations, and that the damage increased with the combined total dose of electrons, protons, ultraviolet and x-ray radiation along with thermal cycling. This paper discusses the testing and evaluation of the retrieved Teflon ® FEP.