No abstract

The ability to store energy on the electric grid would greatly improve its efficiency and reliability while enabling the integration of intermittent renewable energy technologies (such as wind and solar) into baseload supply. Batteries have long been considered strong candidate solutions owing to their small spatial footprint, mechanical simplicity and flexibility in siting. However, the barrier to widespread adoption of batteries is their high cost. Here we describe a lithium-antimony-lead liquid metal battery that potentially meets the performance specifications for stationary energy storage applications. This Li||Sb-Pb battery comprises a liquid lithium negative electrode, a molten salt electrolyte, and a liquid antimony-lead alloy positive electrode, which self-segregate by density into three distinct layers owing to the immiscibility of the contiguous salt and metal phases. The all-liquid construction confers the advantages of higher current density, longer cycle life and simpler manufacturing of large-scale storage systems (because no membranes or separators are involved) relative to those of conventional batteries. At charge-discharge current densities of 275 milliamperes per square centimetre, the cells cycled at 450 degrees Celsius with 98 per cent Coulombic efficiency and 73 per cent round-trip energy efficiency. To provide evidence of their high power capability, the cells were discharged and charged at current densities as high as 1,000 milliamperes per square centimetre. Measured capacity loss after operation for 1,800 hours (more than 450 charge-discharge cycles at 100 per cent depth of discharge) projects retention of over 85 per cent of initial capacity after ten years of daily cycling. Our results demonstrate that alloying a high-melting-point, high-voltage metal (antimony) with a low-melting-point, low-cost metal (lead) advantageously decreases the operating temperature while maintaining a high cell voltage. Apart from the fact that this finding puts us on a desirable cost trajectory, this approach may well be more broadly applicable to other battery chemistries.

h i g h l i g h t s g r a p h i c a l a b s t r a c t Electrochemical behavior of the LieBi system was investigated for liquid metal cells. Lithium insertion kinetics in liquid bismuth were studied in a threeelectrode cell. LijLiCleLiBrjBi cells showed long life, high efficiency, and low fade rate. System scalability demonstrated in prototypes with 10 and 100 times original capacity. Robustness shown by cooling to solidify cell, followed by heating and recycling. a b s t r a c tIn an assessment of the performance of a LijLiCleLiFjBi liquid metal battery, increasing the current density from 200 to 1250 mA cm À2 results in a less than 30% loss in specific discharge capacity at 550 C. The charge and discharge voltage profiles exhibit two distinct regions: one corresponding to a LieBi liquid alloy and one corresponding to the two-phase mixture of LieBi liquid alloy and the intermetallic solid compound, Li 3 Bi. Full cell prototypes of 0.1 Ah nameplate capacity have been assembled and cycled at 3 C rate for over a 1000 cycles with only 0.004% capacity fade per cycle. This is tantamount to retention of over 85% of original capacity after 10 years of daily cycling. With minimal changes in design, cells of 44.8 Ah and 134 Ah capacity have been fabricated and cycled at C/3 rate. After a hundred cycles and over a month of testing, no capacity fade is observed. The coulombic efficiency of 99% and energy efficiency of 70% validate the ease of scalability of this battery chemistry. Post mortem cross sections of the cells in various states of charge demonstrate the total reversibility of the Li 3 Bi solid phase formed at high degrees of lithiation.

No abstract

No abstract

Metals cannot be extracted by electrolysis of transition-metal sulfides because as liquids they are semiconductors, which exhibit high levels of electronic conduction and metal dissolution. Herein by introduction of a distinct secondary electrolyte, we reveal a high-throughput electro-desulfurization process that directly converts semiconducting molten stibnite (Sb2S3) into pure (99.9%) liquid antimony and sulfur vapour. At the bottom of the cell liquid antimony pools beneath cathodically polarized molten stibnite. At the top of the cell sulfur issues from a carbon anode immersed in an immiscible secondary molten salt electrolyte disposed above molten stibnite, thereby blocking electronic shorting across the cell. As opposed to conventional extraction practices, direct sulfide electrolysis completely avoids generation of problematic fugitive emissions (CO2, CO and SO2), significantly reduces energy consumption, increases productivity in a single-step process (lower capital and operating costs) and is broadly applicable to a host of electronically conductive transition-metal chalcogenides.

not Available.