Blends of low‐density polyethylene with random copolymers of ethylene and vinyl acetate (PE/EVA) are studied with respect to their environmental stress‐cracking resistance (ESCR) using the Bell‐telephone test. This system shows the shortest time to failure in the ESCR test after annealing at 50 °C in a stress‐cracking agent (Igepal solution) compared with that in the tests conducted at 30 and 70 °C. The increase of the time to failure at 70 °C as compared with that at 50 °C is probably the result of the semicrystalline proportion of EVA melting. Transmission electron microscopy images (see Figure) reveal that EVA particles are molten and deformed in bending direction of the sample at 70 °C in contrast to samples annealed at 50 and 30 °C. TEM pictures of a failed sample during the test conducted at 50 °C indicate that EVA particles can stop crack propagation.TEM image of PE/EVA‐5.4 after 1 000 h in ESCR test conditions at 70 °C.magnified imageTEM image of PE/EVA‐5.4 after 1 000 h in ESCR test conditions at 70 °C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.