Objective: This study evaluated the effects of alternative self-etch application modes on resin-dentin microtensile bond strength (µTBS) of three commercially available “no wait” concept universal adhesives. Materials and methods: In this study extracted impacted non-carious human third molars were used. The flat surfaces were prepared in mid-coronal dentin and prepared with a 600-grit SiC paper. The three universal adhesives that were used are as follows: Clearfil Universal Bond Quick (CUQ, Kuraray Noritake, Japan), G-Premio Bond (GPB, GC Corp, Japan), and a self-curing universal adhesive “Tokuyama Universal Bond” (TUB; Tokuyama Dental, Japan). The following three different application procedures were used for the dentin surfaces: the adhesives were applied and immediately subjected to air-dry; the adhesives were applied followed by a 10-second wait; or the adhesives were rubbed for 10 seconds. Then composite resin was applied to the dentin surface and light cured. After storage in 37°C distilled water for 24 h, all the bonded teeth were cut into 1mm² sections using a low-speed diamond saw (Micracut 125 Low Speed Precision Cutter, Metkon, Bursa, Turkey) under running water (n=15). The sections were subjected to a tensile force at a crosshead speed of 1mm/min in a testing apparatus (Microtensile Tester, Bisco, IL, USA) and µTBS values were measured. Data were analyzed using the Kruskal-Wallis test and Mann-Whitney U test. Failure modes were analyzed under a stereomicroscope. Results: Prolonged application time significantly affected the µTBS (p<0.005). A significant increase of µTBS on active application was observed for CUQ and GPB. The TUB with an active application had a significantly lower µTBS value compared with the other adhesives. Conclusions: Prolonged application time caused significant improvement of bond strength in all adhesives. The active application is effective at increasing the dentin bond strength except for TUB.
Surface changes of restorative materials after bleaching have clinical importance in terms of the durability and survival of restorations. This study aimed to evaluate the effect of home bleaching on the surface roughness, microhardness, and surface analysis of four different types of chairside computer-aided design and computer-aided manufacturing (CAD/CAM) materials. Specimens were prepared from composite resin (Brilliant Crios: BC), resin nanoceramic (Lava Ultimate: LU), polymer-infiltrated ceramic-network (Vita Enamic: VE), and zirconia-reinforced lithium silicate glass-ceramic (Vita Suprinity: VS) CAD/CAM materials. Specimens were polished using 800, 1000, 1200, and 2000 grit SiC papers. Each restorative material was randomly divided into two groups; control and bleaching (n=10). The 16% carbamide peroxide bleaching agent (Whiteness Perfect 16%, FGM) was applied to the specimens for 4 h/day for 14 days. Surface roughness values (Ra) were obtained using a profilometer, and microhardness values (VHN) were obtained using a Vickers microhardness test. Surface analysis of specimens was evaluated by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX). Data were analyzed Two-way ANOVA and Fisher’s Least Significant Difference (LSD) test (p<0.05). After bleaching, the surface roughness of BC (p<0.001) and VE (p<0.032) significantly increased. Bleaching did not significantly affect the microhardness of CAD/CAM materials. SEM evaluation showed material-dependent surface damages after bleaching procedures. The effect of 16% carbamide peroxide home bleaching agent on surface roughness and microhardness of chairside CAD/CAM materials is material-dependent. Before bleaching, restorative materials should be protected by applying a protective barrier and contact with the bleaching agent should be minimized. Also, after bleaching, the restoration surface should be carefully inspected, and re-polishing might be beneficial.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.