For the first time, a powder of Na3Fe3(PO4)4 was obtained by solid state reaction. It crystallizes in monoclinic space group C2/c in good agreement with previous studies of a single crystal. The Rietveld refinement of the XRD pattern showed line broadening of some diffraction lines associated with size and strain effects. Its layered structure can be described by complex layers of corner-sharing FeO6 octahedra connected by PO4 tetrahedra through corner and edge sharing. The Na+ ions are located in the interslab space. The local environments of Fe, Na, and P were characterized by 57Fe Mössbauer spectroscopy and 23Na and 31P MAS NMR. A Second ORder Graphic Extrapolation (SORGE) diagram as introduced by Massiot et al. allowed us to fully interpret the 23Na MAS NMR spectrum that exhibits three signals for two crystallographic Na sites. The electrochemical properties of Na3Fe3(PO4)4 were tested in sodium cells. Ex situ and in situ X-ray diffraction data and Mössbauer spectroscopy measurements indicate that the intercalation−deintercalation process of Na+ ions in Na3Fe3(PO4)4 is reversible and that the structural framework is maintained during cycling. Some degree of disorder is, however, observed for a large intercalated Na+ amount.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.