Resistance switching (RS) devices with ultra-thin Ta2O5 switching layer (0.5–2.0 nm) with a cell diameter of 28 nm were fabricated. The performance of the devices was tested by voltage-driven current—voltage (I-V) sweep and closed-loop pulse switching (CLPS) tests. A Ta layer was placed beneath the Ta2O5 switching layer to act as an oxygen vacancy reservoir. The device with the smallest Ta2O5 thickness (0.5 nm) showed normal switching properties with gradual change in resistance in I-V sweep or CLPS and high reliability. By contrast, other devices with higher Ta2O5 thickness (1.0–2.0 nm) showed abrupt switching with several abnormal behaviours, degraded resistance distribution, especially in high resistance state, and much lower reliability performance. A single conical or hour-glass shaped double conical conducting filament shape was conceived to explain these behavioural differences that depended on the Ta2O5 switching layer thickness. Loss of oxygen via lateral diffusion to the encapsulating Si3N4/SiO2 layer was suggested as the main degradation mechanism for reliability, and a method to improve reliability was also proposed.
Charge injection meditated switching of the ferroelectric–dielectric bilayer is quantitatively investigated by the compact model and newly introduced pulse measurement.
The chemical, physical, and electrical properties of the atomic layer deposited Hf 0.5 Zr 0.5 O 2 thin films using tetrakis(ethylmethylamino) (TEMA) and tetrakis(dimethylamino) (TDMA) precursors are compared. The ligand of the metal-organic precursors strongly affects the residual C concentration, grain size, and the resulting ferroelectric properties. Depositing Hf 0.5 Zr 0.5 O 2 films with the TDMA precursors results in lower C concentration and slightly larger grain size. These findings are beneficial to grow more ferroelectric-phase-dominant film, which mitigates its wake-up effect. From the wake-up test of the TDMA-Hf 0.5 Zr 0.5 O 2 film with a 2.8 MV/cm cycling field, the adverse wake-up effect was well suppressed up to 10 5 cycles, with a reasonably high double remanent polarization value of 40 μC/cm 2. The film also showed reliable switching up to 10 9 cycles with the 2.5 MV/cm cycling field without involving the wake-up effect but with the typical fatigue behavior.
Ti layer inserted in the TiN gate electrode effectively scavenges the oxygen in the low‐k interfacial SiO2 of the metal–ferroelectric–insulator–semiconductor (MFIS) capacitors with the ferroelectric Al‐doped HfO2 (HAO) thin film. The scavenging effect increases remanent polarization (Pr) and reduces coercive voltage (Vc) and capacitance equivalent thickness (CET) of the HAO films, particularly when the MFIS capacitor is annealed at 800 °C. Additionally, frequency dispersion of capacitance characteristics and interface trap density (Dit) calculations reveal that actively‐triggered oxygen‐scavenging effects also reduce defect or trap‐induced degradation. The Ti‐inserted MFIS structure exhibits fatigue‐free endurance and relatively low leakage current characteristics as compared to a structure without the Ti scavenging layer in high annealing temperature conditions required for crystallization of the HAO ferroelectric films.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.