Material and optical characterizations have been conducted for epitaxially grown Ge1−xSnx thin films on Si with Sn composition up to 10%. A direct bandgap Ge0.9Sn0.1 alloy has been identified by temperature-dependent photoluminescence (PL) study based on the single peak spectrum and the narrow line-width. Room temperature PL emission as long as 2230 nm has also been observed from the same sample.
The GeSn direct gap material system, with Si complementary-metal-oxide semiconductor (CMOS) compatibility, presents a promising solution for direct incorporation of focal plane arrays with short wave infrared detection on Si. A temperature dependence study of GeSn photoconductors with 0.9, 3.2, and 7.0% Sn was conducted using both electrical and optical characterizations from 300 to 77 K. The GeSn layers were grown on Si substrates using a commercially available chemical vapor deposition reactor in a Si CMOS compatible process. Carrier activation energies due to ionization and trap states are extracted from the temperature dependent dark I-V characteristics. The temperature dependent spectral response of each photoconductor was measured, and a maximum long wavelength response to 2.1 μm was observed for the 7.0% Sn sample. The DC responsivity measured at 1.55 μm showed around two orders of magnitude improvement at reduced temperatures for all samples compared to room temperature measurements. The noise current and temperature dependent specific detectivity (D*) were also measured for each sample at 1.55 μm, and a maximum D* value of 1 × 10(9) cm·√Hz/W was observed at 77 K.
Thin-film Ge0.9Sn0.1 structures were grown by reduced-pressure chemical vapor deposition and were fabricated into photoconductors on Si substrates using a CMOS-compatible process. The temperature-dependent responsivity and specific detectivity (D*) were measured from 300 K down to 77 K. The peak responsivity of 1.63 A/W measured at 1.55 μm and 77 K indicates an enhanced responsivity due to photoconductive gain. The measured spectral response of these devices extends to 2.4 μm at 300 K, and to 2.2 μm at 77 K. From analysis of the carrier drift and photoconductive gain measurements, we have estimated the carrier lifetime of this Ge0.9Sn0.1 thin film. The longest measured effective carrier lifetime of 1.0 × 10−6 s was observed at 77 K.
Fully strained and relaxed epitaxial Ge1-xSnx alloys with Sn contents up to 12 at. % have been grown on Ge buffered Si using an Epsilon® 2000 Plus commercial chemical vapor deposition system. Using a specialized growth approach intrinsic, p-type, and n-type alloys have been demonstrated. Material and optical characterization of these alloys indicate that the alloys are of high crystal quality in which the Sn is fully substitutional. Heterostructures of doped Ge/Ge1-xSnx/Ge have also grown to demonstrate their application in light emitting and detecting devices. Phosphorus doped Ge1-xSnx photoluminescence has also been observed at wavelengths up to 2.4 μm. Growth, materials and optical properties of these materials will be discussed.
Temperature-dependent photoluminescence (PL) study has been conducted in Ge1−xSnx films with Sn compositions of 0.9%, 3.2%, and 6.0% grown on Si. The competing between the direct and indirect bandgap transitions was clearly observed. The relative peak intensity of direct transition with respect to the indirect transition increases with an increase in temperature, indicating the direct transition dominates the PL at high temperature. Furthermore, as Sn composition increases, a progressive enhancement of direct transition was observed due to the reduction of direct-indirect valley separation, which experimentally confirms that the Ge1−xSnx could become the group IV-based direct bandgap material grown on Si by increasing the Sn content.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.