The preferred growth direction of cathodic arc physical vapor deposition-produced TiN coatings changes from (1 1 1) to (2 2 0) with high voltage pulsed bias application in the presence of Ar gas. In this study, tribological properties of these coatings were investigated via reciprocating wear tests against an inert counterbody for observing the role of orientation on tribological properties. Friction coefficients and wear of (2 2 0) oriented coatings were observed to be significantly lower compared to (1 1 1) oriented coatings. Micro-Raman investigations of the wear debris formed during tribotest revealed clear differences between (1 1 1) and (2 2 0) oriented films. Wear debris obtained from (2 2 0) oriented coatings consisted of nc TiO2 phases (anatase and rutile) whereas (1 1 1) oriented coatings produced amorphous Ti oxides. This behavior is attributed to the orientation dependent oxidation kinetics of the coatings as verified with isothermal oxidation tests. A mechanism for improved tribological behavior is proposed based on the obtained results.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.