Asphalt pavement is significantly affected by ultraviolet (UV) aging. Therefore, the establishment of an asphalt UV aging evaluation system is desirable for highway construction in areas which experience strong UV radiation. In this study, Dunhuang City in Gansu Province (northwest China) was used as the research site. Base and SBS modified asphalts were selected, and their performance changes before and after UV aging were studied. An asphalt UV aging evaluation system was established, including the conditions for an indoor, accelerated UV aging test as well as evaluation indicators. The results showed that the adverse effect of UV aging on asphalt performance was greater than that of RTFOT and PAV, and that the low-temperature performance of asphalt degraded most rapidly. SBS modified asphalt was more resistant to UV aging than base asphalt, while 60/80 pen grade base asphalt was found to be unsuitable for use on pavements which are exposed to strong UV radiation. The residual penetration, penetration attenuation index at 25 °C, and residual ductility of the asphalt were used as indicators to characterize the aging of asphalt, while the fracture energy method was used as a supplementary evaluation method.
Uneven support as result of voids beneath concrete slabs can lead to high tensile stresses at the corner of the slab and eventually cause many forms of damage, such as cracking or faulting. Three-dimensional (3D) finite element models of the concrete pavement with void are presented. Mesh convergence analysis was used to determine the element type and mesh size in the model. The accuracy of the model is verified by comparing with the calculation results of the code design standards in China. The reliability of the model is verified by field measurement. The analysis shows that the stresses are more affected at the corner of the slab than at the edge. Impact of void size and void depth at the slab corner on the slab stress are similar, which result in the change of the position of the maximum tensile stress. The maximum tensile stresses do not increase with the increase in the void size for relatively small void size. The maximum tensile stress increases rapidly with the enlargement in the void size when the size is ≥0.4 m. The increments of maximum tensile stress can reach 183.7% when the void size is 1.0 m. The increase in slab thickness can effectively reduce maximum tensile stress. A function is established to calculate the maximum tensile stress of the concrete slab. The function takes into account the void size, the slab thickness and the vehicle load. The reliability of the function was verified by comparing the error between the calculated and simulated results.
Dowel bars are arranged between two slabs of jointed plain concrete pavements to transfer load between them. The looseness of these dowel bars leads to the decrease of the load transfer efficiency (LTE). Meanwhile, repeated vehicle load can result in void near the joints. In this paper, the behaviors of concrete pavement under the effect of void size and joint stiffness were studied by using ABAQUS software. The FEA model was calibrated for different element parameters based on mesh convergence analysis and validated by comparison with previous studies. The voids beneath slabs were considered in this study, including the loaded slab and unloaded slab. The different effects of base course modulus on the stress of loaded slab are also analysed. It is concluded that the results show that the void size and joint stiffness affect the stress of the loaded plate. Smaller void size and larger joint stiffness will lead to the maximum stress located at the bottom of the loaded slab, and the void size has little effect on the stress of the loaded slab. Otherwise, the larger void size will cause larger stress. The effect of base modulus on stress is similar.
Uneven support as result of voids beneath concrete slabs can lead to high tensile stresses at the corner of the slab and eventually cause many forms of damage, such as cracking or faulting. Three-dimensional (3D) finite element models of the concrete pavement with void are presented. The accuracy of the model is verified by two methods. The analysis shows that the impact of void size and void depth at the slab corner on the slab stress are similar, which result in the change of the position of the maximum tensile stress. The maximum tensile stresses do not increase with the increase of the void size for relatively small void size. The maximum tensile stress increases rapidly with the enlargement in the void size when the size≥0.4m. The increments of maximum tensile stress can reach 183.7% when the void size are 1.0m. The increase of slab thickness can effectively reduce maximum tensile stress. A function is established to calculate the maximum tensile stress of the concrete slab. The function takes into account the void size and the slab thickness. The reliability of the function was verified by comparing the error between the calculated and simulated results.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.