The paper discusses the comparison of pack carburizing-nitriding SUS 316 with gas Nitrogen. The purpose of this study was to increase the hardness and corrosion resistance of SUS 316. The research used a pack carburizing-nitriding method with gas type Welding Grade (WG) and Ultra High Purity (UHP). The pack carburizing process uses teak wood activated carbon and barium carbonate as a bio-photo catalyst. The specimens were put into a Sealed Steel Container containing teak wood activated carbon, with a depth of 1 cm below the activated carbon's surface. The test material is then heated until it reaches 850 °C and is held for 1 hour in a heating furnace. Furthermore, the nitriding process, the specimen is put into a tightly closed nitrogen tube, then nitrogen gas flows until the pressure reaches 41 bar and is held for 24 hours. They are using Welding Grade (WG) and Ultra High Purity (UHP) gas types. Furthermore, microVickers hardness testing, optical microscope, and Scan Electron Microscope (SEM) were carried out. The results of the study include a. There was an increase in violence by 41.7 % for UHP and WG (17.3 %). b. The formation of nitride compounds and carbon dissipation on the specimen surface in the UHP carburizing-nitriding pack treatment is more than WG. The formation of a nitride layer is indicated by its fine and dense morphology and film bonding to the substrate. The chemical composition affects the diffusivity of nitrogen atoms in modifying the surface layer of the substrate. The higher the nitride compound formed, the smoother the substrate surface. Also, with UHP treatment, the lower the elemental content of Cr makes SUS 316 more resistant to corrosion. So that SUS 316 UHP can be recommended for use as an implant material
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.