Li4Ti5O12 (LTO) exhibits zero-strain behavior, exceptional cycle stability, low cost, and high safety. However, it is still low in electronic and ionic conductivity. Incorporating Sn into LTO materials can increase electronic conductivity and specific capacity. However, Sn still experiences volumetric expansion during the charging/discharging process. Adding activated carbon (AC) into the LTO/Sn composite can help improve the expansion resistance and electronic conductivity. In this work, the AC was first synthesized from charcoals through the carbon activation process and mixed with LTO precursors through the sol-hydrothermal method followed by mixing with Sn through the mechanochemical process to produce LTO@AC/Sn composites. The Sn content was fixed at 15 wt.%, while the AC contents were varied at 1 wt.%, 3 wt.%, and 5 wt.%. The AC specific surface area is increased by more than 100% compared to the non-activated one. The best effects of AC on grain morphology and distribution were found in the LTO/Sn contained 3 wt.% of AC, leading to transfer resistance, ohmic resistance, specific capacity, and coulombic efficiency were found to be 48.1 Ω, 8.5 Ω, 138 mAhg-1, and near 100%, respectively. The result suggests that the LTO@AC/Sn could be a favorable anode active material in lithium-ion batteries.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.