Lead lanthanum zirconate titanate (PLZT) thin films were deposited on r-plane sapphire at low temperatures by RF triode magnetron sputtering using lead compensated hot-pressed targets. To obtain fully perovskite phase in the films, two types of post-deposition processing were investigated: rapid thermal annealing (RTA) and furnace annealing (FA). Dielectric and electro-optic properties of PLZT films were found to be strongly dependent on annealing conditions. The peak dielectric constant of the films were 1200 and 2800 with Curie temperatures of 110 degrees C and 190 degrees C after RTA and FA processing, respectively. The dielectric losses in the films were fairly low; tan deltas were less than 0.02 after RTA and less than 0.04 after FA processing. The films showed good optical transmission characteristics after annealing and an anomalously large effective quadratic electro-optic effect was observed in one furnace annealed film.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.