Duplex stainless steels (DSSs) are complex materials and they have been widely used in the marine environment and gas industries, primarily offering a better resistance of pitting corrosion and good mechanical properties. In the present work, the effects of heat treatment on duplex stainless steel (DSS) weld overlay samples that were heat treated at three different temperatures, namely 350 °C, 650 °C, and 1050 °C, and followed by air cooling and water quenching were studied. Stress relief temperature at 650 °C had induced sigma phase precipitation in between delta ferrite and austenite (δ/γ) grain boundaries, resulting in the loss of corrosion resistance in the weld metal. Interestingly, post weld heat treatment (PWHT) test samples that were reheated to solution annealing temperature had shown no weight loss. The ferrite count determination in the region of weld metal overlay increased at hydrogen relief and decreased at stress relief temperatures due to slow cooling, which is more favorable to austenite formation. The amount of ferrite in the weld metals was significantly reduced with the increment of solution anneal temperature to 1050 °C because of sufficient time for the formation of austenite and giving optimum equilibrium fraction in the welds.
Duplex stainless steel (DSS) has a reasonably high resistance to chloride stress corrosion cracking for offshore and marine applications. However, DSS weld overlay has not been successfully demonstrated due to some inherent problems in achieving pitting and crevice corrosion resistance. In this research work, isothermal heat treatments (350, 650 and 1050 °C) with and different cooling rates have been performed DMR249 Grade A by using shield metal arc welding (SMAW) with an E2209 electrode. Micrographs have shown two phase microstructures of the DSS weld metal, the amounts of austenite phase increased with increment of post-weld heat treatment (PWHT) temperatures. The dilution has maintained consistent values except solution annealing that has shown the disappearance of the heat affected zone in micrographs. The weld metal hardness values increased with PWHT temperatures and remained low at solid solution annealing temperatures. The major alloying elements (C, Mo, Cr, Ni, N, and Fe) were analyzed, as these elements can contribute to intermetallic phases. The results showed that C and Cr content slightly increased with PWHT except for solid solution annealing, Mo showed consistently low content due to dilution effects. Ni maintained higher content, although the heat-treated samples showed slight fluctuations. Nitrogen produced consistent values, as recommended to prevent critical involvement in nitride precipitation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.