The corrosion behavior of TiCode-12 (Ti-0.3 Mo-0.8 Ni) high level nuclear waste container alloy has been studied for a simulated WIPP brine at a temperature of 150°C or below. Crevice corrosion was identified as a potentially important failure mode for this material. Within a mechanical crevice, a thick oxide film was found and shown to be the rutile form of TiO2, with a trace of lower oxide also present. Acidic conditions were found to cause a breakdown of the passive oxide layer. Solution aeration and increased acidity accelerate the corrosion rate. In hydrogen embrittlement studies, it was found that hydrogen causes a significant decrease in the apparent stress intensity level in fracture mechanics samples. Hydride formation is thought to be responsible for crack initiation. Stress corrosion cracking under static loads was not observed. Attention has also been given to methods for extrapolating short term uniform corrosion rate data to extended times.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.