Over-all mechanical properties of alloys are extremely low at the last stage of solidification where alloy exists at brittle temperature range (BTR). When the solidification process is completed a sudden and marked change in strength and ductility of metal is observed. It means that as long as liquid phase is present, metal will fail in a brittle manner. There are known different theories of brittleness of alloys in existence of liquid phase. The idea involved by authors of the paper is as follows: three major factors caused by presence of liquid may be taken into account:-decreasing the energy needed for crack nucleation, -increasing atomic diffusional flux out of the crack tip, -creating a path for abnormally quick diffusion of atoms from the crack tip. Keywords: high temperature brittleness, hot tearing, shrinkage brittleness, mushy state Własności mechaniczne stopów są bardzo niskie w ostatnim stadium krzepnięcia, w którym stop wykazuje kruchość wysokotemperaturową. Przy końcu procesu krzepnięcia obserwuje się nagłą zmianę wytrzymałości i plastyczności metalu. Dopóki występuje faza ciekła metal ulega zniszczeniu w sposób kruchy. Przyczyną tego mogą być trzy główne czynniki związane z obecnością fazy ciekłej: a) spadek energii potrzebnej do zarodkowania pęknięcia, b) wzrost strumienia dyfuzji atomów od wierzchołka pęknięcia, c) utworzenie ścieżki do anomalnie szybkiej dyfuzji atomów od wierzchołka pęknięcia.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.