The renewable biomass material obtained from rice husk, a low-cost agricultural waste, was used as a precursor to synthesize a highly porous graphene-based carbon as electrode material for supercapacitors. Activated graphene-based carbon (AGC) was obtained by a two-step chemical procedure and exhibited a very high specific surface area (SSA) of 3292 m2 g−1. The surface morphology of the synthesized materials was studied using scanning and transmission electron microscopy (SEM, TEM). Furthermore, the AGC was modified with nickel hydroxide Ni(OH)2 through a simple chemical precipitation method. It was found that the most significant increase in capacitance could be reached with Ni(OH)2 loadings of around 9 wt.%. The measured specific capacitance of the pure AGC supercapacitor electrodes was 236 F g−1, whereas electrodes from the material modified with 9 wt.% Ni(OH)2 showed a specific capacitance of up to 300 F g−1 at a current density of 50 mA g−1. The increase in specific capacitance achieved due to chemical modification was, therefore 27%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.