This work demonstrates a simple approach to control the
orientation
of the self-assembled nanostructured block copolymer thin films of
polystyrene-block-polydimethylsiloxane (PS-b-PDMS) by functionalization of the oxide layer (SiO2) on the Si substrate followed by thermal annealing under
low-pressure environmental conditions. The substrate can be functionalized
through two-step grafting of hydroxy-terminated polystyrene brush
(PS–OH brush) followed by hydroxy-terminated polydimethylsiloxane
brush (PDMS–OH brush) onto the wafer substrate. By controlling
the grafting ratio of PS–OH and PDMS–OH brushes, the
affinities of the PS and PDMS blocks with the substrates can be fine-tuned
to provide a neutral substrate in order to form perpendicular cylinders
from the bottom after thermal annealing. Owing to the vacuum-driven
orientation [i.e., thermal annealing under low-pressure
environment conditions (∼10–4 Pa)], the orientation
of the cylinders can be controlled at the air/polymer interface. Interestingly,
by combining the vacuum-driven approach with substrate functionalization,
perpendicular cylinders from the air/polymer interface and substrate/polymer
interface can be generated, respectively. Consequently, well-aligned
perpendicular cylinders with long-range ordering can be fabricated
by the self-alignment process.
This work aims to demonstrate a facile method for the
controlled
orientation of nanostructures of block copolymer (BCP) thin films.
A simple diblock copolymer system, polystyrene-block-polydimethylsiloxane (PS-b-PDMS), is chosen to
demonstrate vacuum-driven orientation for solving the notorious low-surface-energy
problem of silicon-based BCP nanopatterning. By taking advantage of
the pressure dependence of the surface tension of polymeric materials,
a neutral air surface for the PS-b-PDMS thin film
can be formed under a high vacuum degree (∼10–4 Pa), allowing the formation of the film-spanning perpendicular cylinders
and lamellae upon thermal annealing. In contrast to perpendicular
lamellae, a long-range lateral order for forming perpendicular cylinders
can be efficiently achieved through the self-alignment mechanism for
induced ordering from the top and bottom of the free-standing thin
film.
Herein, this work aims to directly visualize the morphological
evolution of the controlled self-assembly of star-block polystyrene-block-polydimethylsiloxane (PS-b-PDMS)
thin films via in situ transmission electron microscopy (TEM) observations.
With an environmental chip, possessing a built-in metal wire-based
microheater fabricated by the microelectromechanical system (MEMS)
technique, in situ TEM observations can be conducted under low-dose
conditions to investigate the development of film-spanning perpendicular
cylinders in the block copolymer (BCP) thin films via a self-alignment
process. Owing to the free-standing condition, a symmetric condition
of the BCP thin films can be formed for thermal annealing under vacuum
with neutral air surface, whereas an asymmetric condition can be formed
by an air plasma treatment on one side of the thin film that creates
an end-capped neutral layer. A systematic comparison of the time-resolved
self-alignment process in the symmetric and asymmetric conditions
can be carried out, giving comprehensive insights for the self-alignment
process via the nucleation and growth mechanism.
This study demonstrates a new technique for controlled orientation of nanostructured block copolymer (BCP) thin films through solvent annealing using polystyrene-blockpolydimethylsiloxane (PS-b-PDMS) as a representative BCP system. A two-step substrate functionalization of an intrinsic oxide layer (SiO 2 ) wafer is performed by using hydroxyl-terminated PS (PS-OH) followed by hydroxyl-terminated PDMS (PDMS-OH). By varying the grafting percentage of the PS and PDMS brushes on the substrate, it is possible to give different degrees of stretching and recoiling of grafted PS and PDMS, respectively, using PS-selective solvent for solvent annealing, resulting in roughness variation; that is termed a responsive functionalized substrate. With the appropriate roughness of the functionalized substrate under solvent annealing, the development of perpendicularly oriented cylinders of PDMS in the nanostructured PS-b-PDMS thin films can be driven from the bottom of the film. Moreover, by taking advantage of air plasma treatment, it is possible to generate a top-capped neutral layer on the film surface, giving induced perpendicular cylinders from the top surface of the thin film after solvent annealing. Consequently, it is possible to attain the formation of film-spanning perpendicular cylinders of PDMS in the PS-b-PDMS thin film under solvent annealing through the selfalignment process of the perpendicularly oriented cylinders from the top and the bottom surface of the thin film.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.