The AFM colloidal probe technique was used to measure the interaction between microsized silica spheres and annealed polyelectrolyte brushes made of poly(acrylic acid) (PAA) and poly(2-vinyl pyridine) (P2VP) in KCl solutions of various pH values and salt concentrations. The interaction energy showed a distance dependence that was affected strongly by the swelling and the electric properties of the brushes. Between PAA brushes and silica particles, a repulsive interaction has been observed for all pH values and salt concentrations reflecting the swelling of the brush with varying pH value and the transition from osmotic to salted brush regime with increasing KCl concentration. Force measurements between P2VP brushes and silica particles revealed a much more complex behavior: a steric repulsion by the swollen brush at low pH values, a complex interplay of attractive and repulsive forces at intermediate pH values and a short-ranged attraction between the collapsed brush and the silica particle at basic pH values and high salt concentrations. The results are interpreted in comparison with the Alexander de Gennes model and zeta potential and ellipsometric measurements.

No abstract

No abstract

Forces of interaction within single pairs of poly(2-vinylpyridine) (P2VP) grafted colloids have been measured by optical tweezers (OT) with an extraordinary resolution of ±0.5 pN. Parameters to be varied are the concentration and type of salt (KCl, CaCl2, and LaCl3) of the surrounding medium as well as its pH. The observed force−distance relation is quantitatively described by the Jusufi model [Colloid Polym. Sci. 2004, 282, 910−917] for spherical polyelectrolyte brushes which takes into account the entropic effect of the counterions and enables one to estimate the ionic concentration inside the brush. The transition from an osmotic to the salted brush regime is analyzed in detail. For the scaling of the brush height a power law is found having an exponent of 0.24 ± 0.01, which ranges between the values expected for spherical and planar brushes. At pH 4 a strong transition from a brush to a pancake conformation takes place.

Hydrogels based on poly(N-isopropylacrylamide) (pNIPAAm) exhibit a thermo-reversible volume phase transition from swollen to deswollen states. This change of the hydrogel volume is accompanied by changes of the hydrogel elastic and Young's moduli and of the hydrogel interfacial interactions. To decouple these parameters from one another, we present a class of submillimeter sized hydrogel particles that consist of a thermosensitive pNIPAAm core wrapped by a nonthermosensitive polyacrylamide (pAAm) shell, each templated by droplet-based microfluidics. When the microgel core deswells upon increase of the temperature to above 34 °C, the shell is stretched and dragged to follow this deswelling into the microgel interior, resulting in an increase of the microgel surficial Young's modulus. However, as the surface interactions of the pAAm shell are independent of temperature at around 34 °C, they do not considerably change during the pNIPAAm-core volume phase transition. This feature makes these core-shell microgels a promising platform to be used as building blocks to assemble soft materials with rationally and independently tunable mechanics.

AFM force measurements have been performed to study the influence of the pH value and salt concentration on the interactions between poly(2-vinyl pyridine) brushes and microsized silica spheres, focusing on attractive and adhesion forces. It was found that the interaction was composed of a repulsive component reflecting the conformation of the brush and an additional attractive force. It can therefore be switched reversibly between purely repulsive at pH 2.5 to strong and medium adhesion by changing the pH value to pH 4 and 6, respectively. Addition of KCl showed different effects: at pH 2.5 high salt concentrations induced an attractive force; at pH 4 the interaction changed from strong attraction in the osmotic brush regime to repulsion and weaker adhesion in the salted brush regime; at pH 6 increase of the KCl concentration weakened the attractive force. These effects could partly be explained by the theory of polyelectrolyte brushes; under some conditions the mechanism of the attractive force is still unclear.

No abstract

The response of mixed brushes made of poly(acrylic acid) and poly(2-vinyl pyridine) with a mixing ratio of about 60:40 was studied using atomic force microscopy (AFM) force measurements with colloidal probes and AFM imaging with a sharp tip in the pH range between 2.5 and 8 and at varying KCl concentrations up to 1 M. It was found that under all conditions a dense polyelectrolyte complex layer coexists with excess polyelectrolyte chains in varying swelling states depending on pH and salt concentration. The mixed brush thus combines typical features of polyelectrolyte brushes and complexes. So, the increase of the salt concentration not only led to a transition from osmotic to salted brush regime but also to salt-induced softening or partial decomposition of the complex layer. Attractive forces at high salt concentrations indicated the presence of P2VP chains in the swollen layer even at high pH values.