No abstract

We have measured the temperature-dependent photoluminescence quantum yields (PLQYs) of poly(9, 9-dioctylfluorene) (PFO) films with four morphologies, namely as-spin-coated (SC) glass, quenched nematic glass, crystalline, and vapour-treated SC glass containing a fraction of 21 helix conformation (β-phase) chains. We find that the room temperature PLQYs of the as-SC, crystalline, and quenched films all increase as the temperature is reduced. However, the PLQY of the film containing β-phase chains decreases at temperatures below 150 K. Via temperature-dependent photoinduced absorption measurements, we show that the polaron population in films containing β-phase PFO chains grows as the temperature is reduced, and is significantly larger than in films with any of the other morphologies. Because of the smaller HOMO–LUMO (highest occupied molecular orbital–lowest unoccupied molecular orbital) energy gap of the β-phase chains compared to chains in the surrounding glassy PFO matrix, they act as recombination sites for excitons, and as traps for polarons. Hence at low temperatures, the polarons become strongly localized on these chains, where they quench the singlet excitons and reduce the PLQY.

The origin of electrophosphorescence from a doped polymer light emitting diode ͑LED͒ has been investigated. A luminescent polymer host, poly͑9,9-dioctylfluorene͒ ͑PFO͒, was doped with a red phosphorescent dye, 2,3,7,8,12,13,17,18-octaethyl-21H,23H-porphyrin platinum͑II͒ ͑PtOEP͒. The maximum external quantum efficiency of 3.5% was obtained at a concentration of 4% PtOEP by weight. Energy transfer mechanisms between PFO and PtOEP were studied by absorption, photoluminescence, and photoinduced absorption spectroscopy. Even though electroluminescence spectra were dominated by PtOEP at a concentration of only 0.2 wt % PtOEP, Förster transfer of singlet excitons was weak and there was no evidence for Dexter transfer of triplet excitons. We conclude that the dominant emission mechanism in doped LED's is charge trapping followed by recombination on PtOEP molecules.

Cellular integrity and morphology of most bacteria is maintained by cell wall peptidoglycan, the target of antibiotics essential in modern healthcare. It consists of glycan strands, cross-linked by peptides, whose arrangement determines cell shape, prevents lysis due to turgor pressure and yet remains dynamic to allow insertion of new material, and hence growth. The cellular architecture and insertion pattern of peptidoglycan have remained elusive. Here we determine the peptidoglycan architecture and dynamics during growth in rod-shaped Gram-negative bacteria. Peptidoglycan is made up of circumferentially oriented bands of material interspersed with a more porous network. Super-resolution fluorescence microscopy reveals an unexpected discontinuous, patchy synthesis pattern. We present a consolidated model of growth via architecture-regulated insertion, where we propose only the more porous regions of the peptidoglycan network that are permissive for synthesis.

The bacterial cell wall is essential for viability, but despite its ability to withstand internal turgor must remain dynamic to permit growth and division. Peptidoglycan is the major cell wall structural polymer, whose synthesis requires multiple interacting components. The human pathogen Staphylococcus aureus is a prolate spheroid that divides in three orthogonal planes. Here, we have integrated cellular morphology during division with molecular level resolution imaging of peptidoglycan synthesis and the components responsible. Synthesis occurs across the developing septal surface in a diffuse pattern, a necessity of the observed septal geometry, that is matched by variegated division component distribution. Synthesis continues after septal annulus completion, where the core division component FtsZ remains. The novel molecular level information requires re-evaluation of the growth and division processes leading to a new conceptual model, whereby the cell cycle is expedited by a set of functionally connected but not regularly distributed components.

Surfactant templating is a method that has successfully been used to produce nanoporous inorganic structures from a wide range of oxide-based material. Co-assembly of inorganic precursor molecules with amphiphilic organic molecules is followed first by inorganic condensation to produce rigid amorphous frameworks and then, by template removal, to produce mesoporous solids. A range of periodic surfactant/semiconductor and surfactant/metal composites have also been produced by similar methods, but for virtually all the non-oxide semiconducting phases, the surfactant unfortunately cannot be removed to generate porous materials. Here we show that it is possible to use surfactant-driven self-organization of soluble Zintl clusters to produce periodic, nanoporous versions of classic semiconductors such as amorphous Ge or Ge/Si alloys. Specifically, we use derivatives of the anionic Ge9(4-) cluster, a compound whose use in the synthesis of nanoscale materials is established. Moreover, because of the small size, high surface area, and flexible chemistry of these materials, we can tune optical properties in these nanoporous semiconductors through quantum confinement, by adsorption of surface species, or by altering the elemental composition of the inorganic framework. Because the semiconductor surface is exposed and accessible in these materials, they have the potential to interact with a range of species in ways that could eventually lead to new types of sensors or other novel nanostructured devices.

Progress in the development of generic molecular devices based on responsive polymers is discussed. Characterisation of specially synthesised polyelectrolyte gels, "grafted from" brushes and triblock copolymers is reported. A Landolt pH-oscillator, based on bromate/ sulfite/ferrocyanide, with a room temperature period of 20 min and a range of 3.1 < pH < 7.0, has been used to drive periodic oscillations in volume in a pH responsive hydrogel. The gel is coupled to the reaction and changes volume by a factor of at least 6. A continuously stirred, constant volume, tank reactor was set-up on an optical microscope and the reaction pH and gel size monitored. The cyclic force generation of this system has been measured directly in a modified JKR experiment. The responsive nature of polyelectrolyte brushes, grown by surface initiated ATRP, have been characterised by scanning force microscopy, neutron reflectometry and single molecule force measurements. Triblock copolymers, based on hydrophobic end-blocks and either polyacid or polybase mid-block, have been used to produce polymer gels where the deformation of the molecules can be followed directly by SAXS and a correlation between molecular shape change and macroscopic deformation has been established. The three systems studied allow both the macroscopic and a molecular response to be investigated independently for the crosslinked gels and the brushes. The triblock copolymers demonstrate that the individual response of the polyelectrolyte molecules scale-up to give the macroscopic response of the system in an oscillating chemical reaction.

No abstract