In vibrationally resonant sum-frequency generation (VR-SFG) spectra, the resonant signal contains information about the molecular structure of the interface, whereas the nonresonant signal is commonly treated as a background and has been assumed to be negligible on transparent substrates. The work presented here on model chromatographic stationary phases contradicts this assumption. Model stationary phases, consisting of functionalized fused-silica windows, were investigated with VR-SFG spectroscopy, both with and without experimental suppression of the nonresonant response. When samples are moved from CD(3)OD to D(2)O, the VR-SFG spectrum was found to change over time when the nonresonant signal was present but not when the nonresonant signal was suppressed. No effect was seen when the solvent was changed and pressurized to 900 psi. These results suggest that the response to the new solvent manifests primarily in the nonresonant response, not the resonant response. Any structural changes caused by the new solvent environment appear to be minor. The nonresonant signal is significant and must be properly isolated from the resonant signal to ensure a correct interpretation of the spectral data. Curve-fitting procedures alone are not sufficient to guarantee a proper interpretation of the experimental results.

No abstract

Aluminum plasmonic nanocrescent antennas were fabricated over large substrate areas by incorporating a sacrificial copper layer in nanosphere template lithography (NTL). The addition of the copper mask eliminates the argon ion milling step in the NTL process that is challenging to implement for aluminum nanostructures because of the robust native oxide layer. The aluminum nanocrescents exhibit polarization-dependent localized surface plasmon responses that can be tuned from the near-infrared into the ultraviolet, a region that is difficult to access with more typically used gold and silver. Finite-difference time-domain simulations predict the observed multimodal plasmonic behavior of these aluminum structures. This simple fabrication process will facilitate the implementation of the aluminum nanocrescent antennas in long and short wavelength surface-enhanced spectroscopies, fluorescence lifetime reduction processes, and photocatalysis.

Much research has been done using polymer and silica particles as support materials for catalytically active noble metal nanoparticles, but these materials have limited stability in organic solvents or under extreme reaction conditions such as high pH. Here we present a robust and versatile composite polymer-diamond support for ultrasmall noble metal nanoparticles combining chemical and mechanical stability of diamond with the chemical versatility of a polymer. By exploiting the rich surface chemistry of nanodiamond and incorporating a reactive thiol−ene polymer, a thinly coated polymer-diamond composite was formed. Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and thermogravimetric analysis (TGA) confirmed the presence of the polymer. High resolution scanning transmission electron microscopy (S/TEM) analysis showed that in situ growth of gold, platinum and palladium nanoparticles produced high density coverage at the polymer-diamond support surface. Energy dispersive spectroscopy mapping and S/TEM imaging indicated spatial alignment of nanoparticles with chemical groups present in the polymer used for particle tethering. The polymer-diamond supported nanoparticles catalyze the NaBH 4 reduction of paranitrophenol to para-aminophenol and possess better stability than silica supports which dissolve at high pH resulting in nanoparticle aggregation. With the high robustness of the diamond and the ability to tailor the monomer combinations, this polymer-diamond support system may be expanded to a wide range of nanoparticle compositions suitable for various reaction conditions.

Back-surface mirrors are needed as reference materials for vibrationally resonant sum-frequency generation (VR-SFG) probing of liquid-solid interfaces. Conventional noble metal mirrors are not suitable for back-surface applications due to the presence of a metal adhesion layer (chromium or titanium) between the window substrate and the reflective metal surface. Using vapor deposited 3-mercaptopropyltrimethoxysilane (MPTMS) as a bi-functional adhesion promoter, gold mirrors were fabricated on fused silica substrates. These mirrors exhibit excellent gold adhesion as determined by the Scotch(®) tape test. They also produce minimal spectroscopic interference in the C-H stretching region (2800-3000 cm(-1)), as characterized by VR-SFG. These mirrors are thus robust and can be used as back-surface mirrors for a variety of applications, including reference mirrors for VR-SFG.