Production of Polylactic acid (PLA)/Polycaprolactone (PCL) bionanocomposite films with various ratios was done by adding nanocrystalline celullose (NCC) from oil palm empty fruit bunches (OPEFB) as a filler. The aim of the research was to find out the effect of PLA/PCL ratio on film thickness, transparency of bionanocomposite films and water vapor permeability or WVP of the film bionanocomposite with addition of the 3% NCC. The PLA/PCL ratio are 1.0/0.0; 0.8/0.2; 0.6/0.4; 0.5/0.5; 0.4/0.6; 0.2/0.8; and 0.0/1.0, prepared with solvent casting method. Characterization of PLA/PCL bionanocomposites film performed was thickness, transparency test and water vapor permeability (WVP) test. The thickness of bionanocomposites film produced were around are about 0.036-0.053 mm, results show that the lower PLA/PCL ratio the thicker film obtained. The highest value of film transparency was obtained at a ratio of 1.0 / 0.0 (81.4% at a wavelength of 550 nm), the smaller the PLA / PCL ratio, the lower the value of transparency. The WVP value of PLA/PCL bionanocomposite films gives a lower value than the WVP value of pure PLA film and pure PCL film. The best WVP was obtained at a PLA/PCL ratio of 0.8/0.2 which was 1.49x10-16kg.m/(m2.s.Pa).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.