A series of phenolphthalein-based poly(arylene ether sulfone nitrile)s (PESN) multiblock copolymers containing 1-methylimidazole groups (ImPESN) were synthesized to prepare anion exchange membranes (AEMs) for alkaline fuel cells. The ion groups were introduced selectively and densely on the unit of phenolphthalein as the hydrophilic segments, allowing for the formation of ion clusters. Strong polar nitrile groups were introduced into the hydrophobic segments with the intention of improving the dimensional stability of the AEMs. A well-controlled multiblock structure was responsible for the well-defined hydrophobic/hydrophilic phase separation and interconnected ion-transport channels, as confirmed by atomic force microscopy and small angle X-ray scattering. The ImPESN membranes with low swelling showed a relatively high water uptake, high hydroxide ion conductivity together with good mechanical, thermal and alkaline stability. The ionic conductivity of the membranes was in the range of 3.85-14.67×10(-2) S·cm(-1) from 30 to 80 °C. Moreover, a single H2/O2 fuel cell with the ImPESN membrane showed an open circuit voltage of 0.92 V and a maximum power density of 66.4 mW cm(-2) at 60 °C.

With the intention of optimizing the performance of anion-exchange membranes (AEMs), a set of imidazolium-functionalized poly(arylene ether sulfone)s with densely distributed long flexible aliphatic side chains were synthesized. The membranes made from the as-synthesized polymers are robust, transparent, and endowed with microphase segregation capability. The ionic exchange capacity (IEC), hydroxide conductivity, water uptake, thermal stability, and alkaline resistance of the AEMs were evaluated in detail for fuel cell applications. Morphological observation with the use of atomic force microscopy and small-angle X-ray scattering reveals that the combination of high-local-density-type and side-chain-type architectures induces distinguished nanophase separation in the AEMs. The as-prepared membranes have advantages in effective water management and ionic conductivity over traditional main-chain polymers. Typically, the conductivity and IEC were in the ranges of 57.3-112.5 mS cm(-1) and 1.35-1.84 mequiv g(-1) at 80 °C, respectively. Furthermore, the membranes exhibit good thermal and alkaline stability and achieve a peak power density of 114.5 mW cm(-2) at a current density of 250.1 mA cm(-2). Therefore, the present polymers containing clustered flexible pendent aliphatic imidazolium promise to be attractive AEM materials for fuel cells.

No abstract

No abstract

No abstract