Porous conduits provide a protected pathway for nerve regeneration, while still allowing exchange of nutrients and wastes. However, pore sizes >30 µm may permit fibrous tissue infiltration into the conduit, which may impede axonal regeneration. Coating the conduit with Fibrin Glue (FG) is one option for controlling the conduit’s porosity. FG is extensively used in clinical peripheral nerve repair, as a tissue sealant, filler and drug-delivery matrix. Here, we compared the performance of FG to an alternative, hyaluronic acid (HA) as a coating for porous conduits, using uncoated porous conduits and reverse autografts as control groups. The uncoated conduit walls had pores with a diameter of 60 to 70 µm that were uniformly covered by either FG or HA coatings. In vitro, FG coatings degraded twice as fast as HA coatings. In vivo studies in a 1 cm rat sciatic nerve model showed FG coating resulted in poor axonal density (993 ± 854 #/mm2), negligible fascicular area (0.03 ± 0.04 mm2), minimal percent wet muscle mass recovery (16 ± 1 in gastrocnemius and 15 ± 5 in tibialis anterior) and G-ratio (0.73 ± 0.01). Histology of FG-coated conduits showed excessive fibrous tissue infiltration inside the lumen, and fibrin capsule formation around the conduit. Although FG has been shown to promote nerve regeneration in non-porous conduits, we found that as a coating for porous conduits in vivo, FG encourages scar tissue infiltration that impedes nerve regeneration. This is a significant finding considering the widespread use of FG in peripheral nerve repair.Graphical Abstract
In the 1970s, morphological evidence collected by electron microscopy linked mineral deposition (“calcification” or “mineralization”) in newly-forming bone to membrane-encapsulated particles of a diameter of approximately 100 nm (50–200 nm) that were called “matrix vesiscles”. As the characterisation of these vesicles progressed towards their biochemical composition, the role of lipids in the biomineralization process appeared to be crucial. In particular, a group of cell-membrane phospholipids were identified as major players in the crystal formation process. Indeed, in the 1980s it became clear that phosphatidylserine, together with proteins of the annexin family, was among the most important molecules in binding calcium ions and that this phospholipid was involved in the regulation of the early stages of mineralization in vivo. During the same period of time, the number of surgical implantations of orthopaedic, dental and maxilo-facial devices requiring full integration with the treated bone prompted the study of new functionalisation molecules able to establish a stable bonding with the mineral phase of the host tissue. In the late 1990s studies started that aimed at exploiting the potential of calcium-binding phospholipids and, in particular, of the phosphatidylserine as functionalisation molecules to improve the osteointegration of artificial implants. Later, papers have been published that show the potential of the phophatidylserine and phosphatidylserine-mimicking coating technology to promote calcification both in vitro and in vivo. The promising results support the future clinical application of these novel osteointegrative biomaterials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.