The key importance of the sign of the stress-optic anisotropy ratio for reducing thermally induced depolarization in cubic crystals with 432, 4¯3m and m3m symmetry is addressed. A simple method for measuring the stress-optic anisotropy ratio (including its sign) was proposed and verified in CaF<₂ and TGG crystals by experiment. The ratio at room temperature for the wavelength 1076 nm was measured to be -0.47 and + 2.25, respectively. In crystals with a negative value of this parameter thermally induced depolarization may be reduced significantly by choosing crystal orientation. In a CaF₂ crystal with the [111] orientation a 20-fold reduction of thermally induced depolarization as compared to the [001] orientation was obtained in experiment, which is very promising for using CaF₂ as an active element in high-average-power lasers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.