Antibacterial layer-by-layer coatings were fabricated on silicone that efficiently prevents Pseudomonas aeruginosa biofilm formation during time beyond the useful lifetime of the currently employed urinary catheters in medical practice. The coatings are composed of intact, highly antibacterial polycationic nanospheres processed from aminated cellulose and bacteria-degrading glycosaminoglycan hyaluronic acid. The importance of incorporating nanoscale structures within bacteria-responsive surface coatings to impart durable antibacterial and self-defensive properties to the medical indwelling devices is highlighted.
Laccase-assisted assembling of hybrid biopolymer-silver nanoparticles and cork matrices into an antimicrobial material with potential for water remediation is herein described. Amino-functional biopolymers were first used as doping agents to stabilize concentrated colloidal dispersions of silver nanoparticles (AgNP), additionally providing the particles with functionalities for covalent immobilization onto cork to impart a durable antibacterial effect. The solvent-free AgNP synthesis by chemical reduction was carried out in the presence of chitosan (CS) or 6-deoxy-6-(ω-aminoethyl) aminocellulose (AC), leading to simultaneous AgNP biofunctionalization. This approach resulted in concentrated hybrid NP dispersion stable to aggregation and with hydrodynamic radius of particles of about 250 nm. Moreover, laccase enabled coupling between the phenolic groups in cork and amino moieties in the biopolymer-doped AgNP for permanent modification of the material. The antibacterial efficiency of the functionalized cork matrices, aimed as adsorbents for wastewater treatment, was evaluated against Escherichia coli and Staphylococcus aureus during 5 days in conditions mimicking those in constructed wetlands. Both intrinsically antimicrobial CS and AC contributed to the bactericidal effect of the enzymatically grafted on cork AgNP. In contrast, unmodified AgNP were easily washed off from the material, confirming that the biopolymers potentiated a durable antibacterial functionalization of the cork matrices.
The homogeneous conversion of cellulose dissolved in N-methyl-2-pyrrolidone/LiCl and 1-Nbutyl-3-methylimidazolium chloride with N-methyl-2-pyrrolidone, e-caprolactam, N-methyl-e-caprolactam, and N-methyl-2-piperidone in the presence of p-toluenesulphonic acid chloride was studied. Depending on the reaction conditions, novel cellulose esters with degree of substitution (DS) values ranging from 0.12 to 1.17 could be prepared. The structure of the amino group containing cellulose esters was elucidated by elemental analysis, FTIR-and NMR spectroscopy. NMR spectroscopy revealed an almost complete esterification of position 6 of the anhydroglucose unit at DS of 1. The conversion can be conducted between room temperature and 40°C, while side-reactions became predominant at 60°C. Starting with DS of 0.24, the samples were soluble both in water and dimethyl sulphoxide. The derivatives described are capable of forming polyelectrolyte complexes. The samples were stable at room temperature in aqueous solution at pH 2 and 7. Lower viscosities were found for samples with higher DS in aqueous solution at comparable molar mass.
Photoactive derivatives of cellulose were prepared by a mild esterification of the biopolymer with 2-[(4-methyl-2-oxo-2H-chromen-7-yl)oxy]acetic acid via the activation of the carboxylic acid with N,N 0 -carbonyldiimidazole. Subsequently, modification with the cationic carboxylic acid (3-carboxypropyl)trimethylammonium chloride was carried out. Thus, water soluble polyelectrolytes decorated with high amounts of photochemically active chromene moieties were obtained. The structures of the novel polysaccharide esters and the polyelectrolytes were evaluated by means of NMR and IR spectroscopy. Moreover, the light triggered photodimerization of the chromene moieties of the photoactive polyelectrolytes was studied by means of UV-Vis spectroscopy in the dissolved state. The photochemistry observed may be used to control the properties of the new polysaccharide derivatives and are thus of interest in the design of smart materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.