As is known from the classic works on open pit mining, the bench is a separately developed part of the rock layer, having the form of a step. It should also be noted that it is necessary to clearly differentiate the concepts of “bench height” and “height of the layer to be removed.” The benches are often divided into subbenches, developed by different excavation equipment or by the same equipment both sequentially and simultaneously, but having transport routes that are uniform for the bench. As an example, an excavator stripping of the upper and lower subbenches with loading, respectively, at the level of the excavator and above this level, is usually given, that is, the transport route (road) passes through an intermediate platform bench located in the middle of its height. Therefore, the excavation layer of any height, which is, in fact, a part of the working bench, can be considered as an independent bench with all its attributes, but in order to avoid duplication of definitions, this paper suggests the name “extraction layer”. When developing this element various digging modes can be applied. In this paper, we studied the main modes and selected the one that provides the highest performance.
В условиях рыночной экономики значительное подорожание тарифов на перевозку качественных сырьевых материалов и энергоресурсов на технологические нужды требует разработки более экономичных и экологически чистых стеновых материалов массового применения. Вместе с тем в стране остро возникает вопрос, связанный с дефицитом природного минерального сырья, используемого для данного вида производства строительных материалов. Решением этой проблемы может стать вовлечение в сырьевую базу минеральных промышленных отходов, а также нетрадиционных материалов природной и техногенной основы. Показана возможность получения силикатного стенового материала неавтоклавного твердения на основе вскрышной горелой породы угледобычи и извести месторождений Республики Тыва. Вскрышные горелые породы угледобычи (глиежи) Чаданского угольного разреза представлены плотными породами аргиллитоалевролитового происхождения, по составу близки к алюмосиликатному сырью с высоким содержанием оксидов кремния и алюминия. В качестве вяжущего использована воздушная известь, полученная обжигом местного известняка -месторождение Хайыраканское, которая относится к первому сорту по содержанию оксида кальция CaO более 90 %. Выявлено влияние различных технологических факторов на свойства получаемого материала -оптимальное содержание вяжущего в составе смеси, влажность состава смеси, величина давления прессования и условия твердения получаемых изделий. Установлено, что в зависимости от химико-минералогического и гранулометрического состава сырьевой смеси силикатный стеновой материал с улучшенными свойствами (прочность более 15 МПа) получается при содержании извести 30 % с прессованием сырца (30 МПа) и последующим твердением во влажной среде с тепловлажностной обработкой. Ключевые слова: горелые вскрышные породы, глиежи, известь, технологические факторы, свойстваIn a market economy, a significant increase in prices for the transportation of high-quality raw materials and energy resources for technological needs requires the development of more economical and environmentally friendly wall materials for mass use. At the same time, in the country there is an acute question related to the deficit of needs of natural mineral raw materials used for this type of production of building materials. The solution to this problem can be to the involvement of mineral industrial waste as well as non-traditional materials of natural and man-made bases in the raw material base. The possibility of receiving silicate wall material of not autoclave curing on the basis of overburden burned breed of coal mining and lime of fields of the Republic of Tuva is shown. Overburden burnt rocks of coal mining (gliese) of the Chadan coal mine are represented by dense rocks of argillitesiltstone origin in composition close to aluminosilicate raw materials with a high content of silicon and aluminum oxides. The binder was air lime, obtained by calcining local limestone Hairakan deposit, which belongs to the first grade with a calcium oxide content of CaO of more than 90 %. Influence of various tech...
Показано, что при получении силикатных стеновых материалов на основе песчаниковых вскрышных пород угледобычи и извести, на прочность получаемых изделий влияют величина удельного давления прессования и условия твердения. Выявлено, что для шихты на основе песчаника содержащего 70–75% SiO2 и 30% извести, максимальная прочность получаемого материала достигается при удельном давлении 30 МПа и тепловлажностной обработке при температуре 85–90°С в течении 8 часов и последующем хранении во влажной среде. The article shows that when obtaining silicate wall materials based on sandstone overburden rocks of coal mining and lime, the strength of the resulting products is affected by the value of the specific pressing pressure and the hardening condition.It is revealed that for a batch based on sandstone containing 70–75% of SiO2 and 30% of lime, the maximum strength of the resulting material is achieved at a specific pressure of 30 MPa and heat-and-moisture treatment at a temperature of 85–90°C for eight hours and subsequent storage in a humid environment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.