Analytical solutions of and experimental results on the oxidation kinetics of carbon in a pore are presented. Reaction rate, reaction sequence, oxidant partial pressure, total system pressure, pore/crack dimensions, and temperature are analyzed with respect to the influence of each on an overall linear‐parabolic rate relationship. Direct measurement of carbon recession is performed using two microcomposite model systems oxidized in the temperature range of 700° to 1200°C, and for times to 35 h. Experimental results are evaluated using the derived analytical solutions. Implications on the oxidation resistance of continuous‐fiber‐reinforced ceramic‐matrix composites containing a carbon constituent are discussed.

The NASA Glenn Research Center is developing both a novel cell design (BSC) and a novel ceramic fabrication technique to produce fuel cells predicted to exceed a specific power density of 1.0 kW/kg. The NASA Glenn cell design has taken a completely different approach among planar designs by removing the metal interconnect and returning to the use of a thin, doped LaCrO 3 interconnect. The cell is structurally symmetrical. Both electrodes support the thin electrolyte and contain micro-channels for gas flow--a geometry referred to as a bi-electrode supported cell or BSC. The cell characteristics have been demonstrated under both SOFC and SOE conditions. Electrolysis tests verify that this cell design operates at very high electrochemical voltage efficiencies (EVE) and high H 2 O conversion percentages, even at the low flow rates predicted for closed loop systems encountered in unmanned aerial vehicle (UAV) applications. For UAVs the volume, weight and the efficiency are critical as they determine the size of the water tank, the solar panel size, and other system requirements. For UAVs, regenerative solid oxide fuel cell stacks (RSOFC) use solar panels during daylight to generate power for electrolysis and then operate in fuel cell mode during the night to power the UAV and electronics. Recent studies, performed by NASA for a more electric commercial aircraft, evaluated SOFCs for auxiliary power units (APUs). System studies were also conducted for regenerative RSOFC systems. One common requirement for aerospace SOFCs and RSOFCs, determined independently in each application study, was the need for high specific power density and volume density, on the order of 1.0 kW/kg and greater than 1.0 kW/L. Until recently the best reported performance for SOFCs was 0.2 kW/kg or less for stacks. NASA Glenn is working to prototype the light weight, low volume BSC design for such high specific power aerospace applications.

Carbon fiber‐reinforced silicon carbide (C/SiC) composites have the potential to be utilized in many high‐temperature structural applications, particularly in aerospace. However, the susceptibility of the carbon fibers to oxidation has hindered the composite's use in long‐term reusable applications. In order to identify the composites limitations, fundamental oxidation studies were conducted to determine the effects of such variables as temperature, environment, and stress. The systematic studies first looked at the oxidation of the plain, uncoated carbon fiber, then when fiber was utilized within a C/SiC composite, and finally when a stress was applied to the C/SiC composite (stressed oxidation). The first study, oxidation of just the carbon fibers, showed that the fiber oxidation kinetics occurs in two primary regimes: chemical reaction control and diffusion control. The second study, oxidation of the C/SiC composite, showed the self‐protecting effects from the SiC matrix at elevated temperatures when the composite was not stressed. The final study, stressed oxidation of the C/SiC composite, more closely simulated application conditions in which the material is expected to encounter thermal and mechanical stresses. The applied load and temperature will affect the openings of the as‐fabricated cracks, which are an unavoidable characteristic of C/SiC composites. The main objective of the paper was to determine the oxidation kinetic regimes for the oxidation of carbon fibers in a cracked silicon carbide matrix under stressed and unstressed conditions. The studies help to provide insights in to the protective approaches, that could be used to prevent oxidation of the fibers within the composite.

Ten different ceramic matrix composite (CMC) materials were subjected to a constant load and temperature in an air environment. Tests conducted under these conditions are often referred to as stressed oxidation or creep rupture tests. The stressed oxidation tests were conducted at a temperature of 1454°C at stresses of 69 MPa, 172 MPa and 50% of each material's ultimate tensile strength. The ten materials included such CMCs as C/SiC, SiC/C, SiC/SiC, SiC/SiNC and C/C. The time to failure results of the stressed oxidation tests will be presented. Much of the discussion regarding material degradation under stressed oxidation conditions will focus on C/SiC composites. Thermogravimetric analysis of the oxidation of fully exposed carbon fiber (T300) and of C/SiC coupons will be presented as well as a model that predicts the oxidation patterns and kinetics of carbon fiber tows oxidizing in a nonreactive matrix.