The aim of this study was to determine the degradation resistance of three new formulations-silorane-, Ormocer-and dimer-acidbased materials-and compare them to the traditional dimethacrylatebased materials. One silorane-(Filtek P90, P90), one Ormocer-(Ceram-X, CX), one dimer-acid-(N'Durance, ND) and two dimethacrylate-based (Filtek P60, P60; Tetric Ceram, TC) materials were investigated. Water sorption (Wsp) and solubility (Wsl) were determined after the materials were immersed in water for 28 days. Knoop hardness (KH) was determined before and after 24 h immersion in pure ethanol. The flexuralstrength (FS) was determined by the bending test after one-week storage in a dry environment or after one-week immersion in pure ethanol. Data were submitted to analysis of variance (ANOVA) and Tukey's test (95%). The three new formulations showed lower Wsp than the dimethacrylatebased formulation. CX (0.50 ± 0.17%) and ND (0.72 ± 0.19%) exhibited the lowest Wsp, whereas P90 (0.02 ± 0.03%) and P60 (0.04 ± 0.03%) showed the lowest Wsl. All resins showed reduced Knoop hardness number (KHN) after ethanol immersion. P60 presented the lowest decrease in KH value (19 ± 5%). TC (48 ± 3%) and P90 (39 ± 9%) showed the highest KHN decrease after ethanol storage. The FS of CX, ND and TC were affected by ethanol storage. The new formulations did not improve the degradation resistance, as compared with the traditional methacrylatebased materials.

The time interval between handling and photoactivation significantly influenced the degree of conversion and water sorption of the resin-based cements. In general, one can say that the self-adhesive resin cements should be photoactivated as soon as possible after the material handling process.