Bimetallic Pt–Pd catalysts supported on ceria have been prepared by mechanochemical synthesis and tested for lean methane oxidation in dry and wet atmosphere. Results show that the addition of platinum has a negative effect on transient light-off activity, but for Pd/Pt molar ratios between 1:1 and 8:1 an improvement during time-on-stream experiments in wet conditions is observed. The bimetallic samples undergo a complex restructuring during operation, starting from the alloying of Pt and Pd and resulting in the formation of unprecedented “mushroom-like” structures consisting of PdO bases with Pt heads as revealed by high-resolution transmission electron microscopy (HRTEM) analysis. On milled samples, these structures are well-defined and observed at the interface between palladium and ceria, whereas those on the impregnated catalyst appear less ordered and are located randomly on the surface of ceria and of large PdPt clusters. The milled catalyst prepared by first milling Pd metal and ceria followed by the addition of Pt shows better performances compared to a conventional impregnated sample and also to a sample obtained by inverting the Pd–Pt milling order. This has been ascribed to the intimate contact between Pd and CeO2 generated at the nanoscale during the milling process.

Efficiently treating methane emissions in transportation remains a challenge. Here, we investigate palladium and platinum mono- and bimetallic ceria-supported catalysts synthesized by mechanical milling and by traditional impregnation for methane total oxidation under dry and wet conditions, reproducing those present in the exhaust of natural gas vehicles. By applying a toolkit of in situ synchrotron techniques (X-ray diffraction, X-ray absorption and ambient pressure photoelectron spectroscopies), together with transmission electron microscopy, we show that the synthesis method greatly influences the interaction and structure at the nanoscale. Our results reveal that the components of milled catalysts have a higher ability to transform metallic Pd into Pd oxide species strongly interacting with the support, and achieve a modulated PdO/Pd ratio than traditionally-synthesized catalysts. We demonstrate that the unique structures attained by milling are key for the catalytic activity and correlate with higher methane conversion and longer stability in the wet feed.