Aim of the study was to compare the trimming and non-trimming variants of the microtensile technique with the 'micro' push-out test in the ability to measure accurately the bond strength of fiber posts luted inside root canals. In 15 endodontically treated teeth (Group A), fiber posts were cemented with Excite DSC in combination with Variolink II (Ivoclar-Vivadent). In 15 roots RelyX Unicem (3M-ESPE) was used for fiber post luting (Group B). Within each group, the bond strength of cemented fiber posts was assessed with the trimming and non-trimming microtensile technique, as well as with the push-out test. The great number of premature failures (16.9% in Group A, 27.5% in Group B) and the finding of high standard deviation values make questionable the reliability of the trimming microtensile technique. With the non-trimming microtensile technique, only five sticks were obtained from a total of six roots. The remaining specimens failed prematurely during the cutting phase. With the push-out test no premature failure occurred, the variability of the data distribution was acceptable, and regional differences in bond strength among root levels could be assessed. Relatively low values of bond strength were, in general, recorded for luted fiber posts. In conclusion, when measuring the bond strength of luted fiber posts, the push-out test appears to be more dependable than the microtensile technique.
This study tested the null hypothesis that the use of dentin adhesives produces no improvement on the fixation of fiber posts with resin cements in endodontically treated teeth. Post spaces were prepared in 36 single-rooted root-filled teeth. Silanized glass fiber posts were cemented to the post spaces using a self-etch (ED primer/Panavia 21) and a total etch resin cement (Excite DSC/Variolink II), with or without the accompanying dentin adhesives. Fixation strengths and interfacial ultrastructure were evaluated using a "thin slice" push-out test and transmission electron microscopy. For both resin cements, the fixation strengths obtained from specimens luted with resin cement only did not differ significantly from those in which the intraradicular dentin was first bonded with a dentin adhesive. In the presence of incomplete smear layer removal and interfacial gaps, the dislocation resistance of bonded fiber posts was contributed largely by sliding friction.
Bulk filling resin composite with 1% linear polymerization shrinkage negatively affected the mechanical behavior of class II MOD restored teeth. Class II MOD direct resin composite showed greater potential for damage because of higher internal and marginal stress evolution during resin polymerization shrinkage. With a large class II MOD cavity an indirect composite or a lithium disilicate inlay restoration may provide a mechanical response close to that of a sound tooth.
Clinical RelevanceUse of the centripetal open-sandwich technique may allow for placement of a Class II resin composite restoration with better marginal adaptation, fewer voids and reduced microleakage than the closed sandwich technique.
SUMMARYPurpose: This study evaluated whether a Class II restoration in a flowable resin composite has to be placed prior to (open-sandwich technique) or after (closed-sandwich technique) construction of the interproximal wall in the centripetal build-up technique in order to reduce microleakage. Methods and Materials: Thirty non-carious molars were selected and randomly divided into two groups (n=15). A standardized Class II preparation was made with the cervical margin 1 mm below the cementum-enamel junction. In Group 1, flowable resin composite was applied as a 1 mm base, remaining exposed at the cervical margin. In Group 2, the hybrid resin composite was applied to the interproximal wall, followed by a layer of flowable composite on the pulpal floor, away from the margins. The restorations were then subjected to 500 thermal cycles, each with a dwell time of 20 seconds at 5°C and 55°C. Adaptation at the cervical margin was evaluated by dye penetration and SEM analysis using the replica technique. The data were statistically analyzed using the MannWhitney U-test (p<0.05). Results: The centripetal open-sandwich technique led to significantly lower dye penetration than the centripetal closedsandwich technique (p<0.001). Conclusion:
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.