The purpose of the present study was to evaluate in vitro the degree of marginal leakage in Class V cavities involving the cementoenamel junction. Cavities were 4 mm wide and 2 mm deep. The specimens received dentin pretreatment (37% phosphoric acid) followed by the Single Bond (3M) adhesive system application. The 40 specimens were then divided into four groups: Group 1 (control); Group 2 (Nd:YAG laser at 120 mJ/pulse, frequency of 10 Hz, power of 1.2 W); Group 3 (Nd:YAG laser at 140 mJ/pulse, frequency of 10 Hz, power of 1.4 W); Group 4 (Nd:YAG laser at 160 mJ/pulse, frequency of 10 Hz, power of 1.6 W). The cavities were restored with Z100 composite resin (3M) and light cured at 300-600 mW/cm 2 light intensity. Specimens were thermocycled to 500 cycles from 2-50°C. After that, they were dried and sealed with nail varnish, respecting 1 mm around the restorations, and immersed in 0.5% methylene blue solution for 4 h. After this period, the teeth were rinsed, dried, sectioned, and analyzed in a stereoscopic loupe. The highest leakage scores were considered for each specimen. The results were statistically analyzed by the analysis of variance (ANOVA) -Kruskal-Wallis test to the 5% level. For both the enamel and cementum, there was a decrease in marginal leakage with the application of laser energy; no significant differences were observed for Groups 2, 3, and 4. The results also showed a smaller tendency to marginal leakage on the cementum than on the enamel.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.