A series of cation-exchange membranes were obtained by photoinitiated grafting of acrylic acid onto a polypropylene microporous support having 0.2 µm diameter pores. The poly(acrylic acid) was shown to be contained within the pores of the membrane. The ion-exchange capacities of these "pore-filled" membranes ranged from 65 to 80% of the theoretical values calculated on the basis of their measured graft yields, with water contents ranging from 72 to 77%. The membranes exhibited a chemical valve effect of flux as a function of pH. Treatment of a poly(acrylic acid) grafted membrane with a solution containing ferrous ions resulted in a large uptake of iron (>24% by weight of iron with a membrane containing 152% graft yield of poly(acrylic acid)). Subsequent alkaline (pH 14) oxidation at 70°C with either oxygen or hydrogen peroxide led to the formation of a superparamagnetic nanocrystalline form of ferrihydrite, 5Fe2O3 ·9H2O. The oxide was identified by temperature-dependent Mössbauer spectroscopy recorded from 300 K to 4.2 K. TEM micrographs of sectioned membranes that were treated with H2O2 revealed the presence of two iron oxide morphologies, disk-shaped particles 3-4 nm in diameter and needle-like particles about 4 nm wide and 50 nm long. Only disk-shaped particles were observed in membranes treated with O2. Magnetization measurements indicate that the membranes are superparamagnetic above 50 K with a room temperature magnetization of 3.3 emu g-1 at 20 kOe.Key words: membrane, poly(acrylic acid); iron oxide, magnetic, Mössbauer spectroscopy; magnetization, photografting.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.